Surface-active siloxane photoinitiators

ABSTRACT

Compounds of the fomiula (I) are suitable photoinitiators which accumulates at the surface of the formulation (I), in which R is for example phenyl and A is a surlace-active radical of the formula (III), Y is a divalent group C 3 -C 12 cycloalkylene, C 6 -C 12 bicycloalkylene; C 1 -C 6 alkylenen-C 3 -C 12 cycloalkylene. C 1 -C 6 alkylene-(C 6 -C 12 hicycloalkylene or C 1 -C 10 alkylene interrupted by one or more non-consecutive C 3 -C 12 cycloalkylene, -U-C 3 -C 12 Cycloalkylene, C 6 -C 12 bicycloalkylene or -U-C 6 -C 12 biocycloaIkylene; C 1 -C 10 alkylene interrupted by one or more non-consecutive O and C 3 -C 12 Cycloalkylene, -U-C 3 -C 12 cycloalkylene, C 6 -C 12 bicycloalkylene and/or -U-C 6 -C 12 bicycloalkylene; —(CH 2 ) a —CH—CH 2 —OH or —(CH 2 ) b —O—(CH 2 ) a —CH—CH 2 —OH; or —(CH 2 ) a —CH(OH)—CH 2 — or —(CH 2 ) b —O—(CH 2 ) a  CH(OH)—CH 2 —. U is U′ or U″ U′ is —(CH 2 ) a COO—; U″ is —Si(CH 3 )(CH 3 )— or —(CH 2 ) a —Si(CH 3 )(CH 3 )—, a is a number from 1 to 10; b is a number from 0 to 10; with the proviso that they are, however, at least 1 if the methylene group in question is between two oxygen atoms.

The invention relates to novel surface-active siloxane photoinitiators and to a process for producing stable, scratch-resistant coatings using siloxane photoinitiators as surface-active initiators.

For improving the miscibility (compatibility) of photoinitiators with silicone substrates to be crosslinked photochemically, WO 97/49768, U.S. Pat. No. 5,776,658, U.S. Pat. No. 4,391,963 and EP-A 088842, for example, propose photoinitiators, for example of the hydroxyketone, aminoketone, benzoin ether, benzophenone or thioxanthone type, which have been modified with silyl radicals, including in particular polymeric silyl radicals. Additionally, the patents U.S. Pat. No. 4,536,265, U.S. Pat. No. 4,534,838 and EP-A 162572 describe a wide variety of photoinitiator structures provided with organopolysiloxane radicals. These compounds are, for example, derived from dialkoxyacetophenones and have increased solubility in silicone substrates. U.S. Pat. No. 4,507,187 discloses diketo photoinitiators containing silyl groups as photoinitiators of good solubility in silicone polymers, and also the polymers obtained with these initiators. U.S. Pat. No. 4,477,326 describes self-polymerizing siloxane polymers containing photoinitiators as groups which trigger the polymerization reaction. Polymeric photoinitiators with siloxane radicals are specified in U.S. Pat. No. 4,587,276.

A. Kolar, H. F. Gruber and G. Greber report in J.M.S. Pure Appl. Chem. A31(3) (1994), 305-318 on reactive, silyl-derivatized a-hyfrbxy ketone photoinitiators. The literature references mentioned deal in particular with the solution of the problem of improving the miscibility of the photoinitiators with the substrate that is to be polymerized, i.e. of making the distribution of the initiator within the substrate as homogeneous as possible. WO 98/00456 proposes certain coating compositions and also a curing method by which improved coating surface properties are achieved. Phenylglyoxalate esters having long alkyl ester groups are described, for example, in U.S. Pat. No. 4,024,297.

Within the coatings industry a search is on for new, energy-saving, emissions-minimizing curing mechanisms and applications for preparing stable, scratch-resistant coatings. A particular requirement is to improve the surface of coatings, particularly with regard to hardness, resistance and gloss properties.

It has now been found that the desired properties may be achieved when certain photo-initiators are used in the coatings that are to be cured. For this purpose, the photoinitiator is not distributed as homogeneously as possible in the formulation to be cured but instead accumulates specifically at the surface of the coating to be cured; in other words, there is a specific orientation of the initiator towards the surface of the formulation. To achieve this it is necessary to use specially equipped photoinitiators.

Thus, the invention relates to surface-active siloxane photoinitiators characterized by a siloxane skeleton, which is linked to the glyoxalate moiety via a divalent group Y. The group Y includes a cycloalkylene structure, a bicycloalkylene structure or a group derived from an epoxy derivatization of the siloxane.

The invention relates to surface-active photoinitiators of the formula I

in which

-   -   R is a radical of the formula II     -   or R is naphthyl, anthracyl, phenanthryl or a heterocyclic         radical, the radicals naphthyl, anthracyl, phenanthryl and/or         the heterocycle being unsubstituted or substituted by         C₁-C₈alkyl, phenyl, OR₆, SR₇ and/or NR₈R₉, where the         substituents OR₆, SR₇, NR₈R₉ may form 5- or 6-membered rings via         the radicals R₆, R₇, R₈ and/or R₉ with further substituents on         the naphthyl, anthracyl or phenanthryl ring or on the         heterocycle or with one of the carbon atoms of the naphthyl,         anthracyl or phenanthryl ring or with one of the carbon atoms of         the heterocycle; and         -   R₁, R₂, R₃, R₄ and R₅ independently of one another are             hydrogen; unsubstituted C₁-C₁₂alkyl or C₁-C₁₂alkyl             substituted by OH, C₁-C₄alkoxy, phenyl, naphthyl, halogen,             CN and/or —O(CO)R₁₀; or are C₂-C₁₂alkyl interrupted by one             or more non-successive oxygen atoms; or are OR₆; SR₇; NR₈R₉;             halogen; unsubstituted or C₁-C₄alkyl- and/or             C₁-C₄alkoxy-substituted phenyl, where the substituents OR₆,             SR₇, NR₈R₉may form 5- or 6-membered rings via the radicals             R₆, R₇, R₈ and/or Rg with further substituents on the phenyl             ring or one of the carbon atoms of the phenyl ring;         -   R₆ and R₇ independently of one another are hydrogen;             unsubstituted C₁-C₁₂alkyl or C₁-C₁₂alkyl substituted by OH,             C₁-C₄alkoxy, phenyl, phenoxy and/or —O(CO)R₁₀; or are             C₂-C₁₂alkyl interrupted by one or more non-successive oxygen             atoms; or are unsubstituted phenyl, C₃-C₆alkenyl,             cyclopentyl, cyclohexyl or naphthyl; or are C₁-C₄alkoxy-,             phenyl- and/or C₁-C₄alkyl-substituted phenyl, C₃-C₆alkenyl,             cyclopentyl, cyclohexyl or naphthyl;         -   R₈ and R₉ independently of one another are hydrogen;             unsubstituted C₁-C₁₂alkyl or C₁-C₁₂alkyl substituted by OH,             C₁-C₄alkoxy and/or phenyl; or are C₂-C₁₂alkyl interrupted by             one or more non-successive oxygen atoms; or are phenyl,             —(CO)R₁₀ or SO₂R₁₁; or R₈ and R₉, together with the nitrogen             atom to which they are attached, form a 5-, 6- or 7-membered             ring which is uninterrupted or interrupted by —0— or —NR₁₂—;         -   R₁₀ is C₁-C₈alkyl; unsubstituted phenyl; or phenyl             substituted by C₁-C₄alkyl and/or C₁-C₄alkoxy;         -   R₁₁ is C₁-C₁₂alkyl, unsubstituted phenyl or phenyl             substituted by C₁-C₄alkyl;         -   R₁₂ is hydrogen; unsubstituted C₁-C₈alkyl; C₁-C₈alkyl             substituted by OH or C₁-C₄alkoxy; unsubstituted phenyl;             phenyl substituted by OH, C₁-C₄alkyl and/or C₁-C₄alkoxy; and     -   s is a number from 1 to 1000;     -   A if sis1,         -   A is a surface-active radical of the formula III             in which the units IIIa, IIIb and/or IIIc             are distributed randomly or in blocks; and         -   G₁ is C₁-C₁₈alkyl or a radical of the formula         -   G₂ is C₁-C₁₈alkyl or a radical of the formula             with the proviso that, ift G₂=alkyl, the radical G₂ is             attached directly to the silicon atom without an oxygen             bridge;         -   R₁₃, R₁₄, R₁₅, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁ and R₂₂ independently             of one another are C₁-C₁₈alkyl, phenyl, C₂-C₆hydroxyalkyl,             C₂-C₆aminoalkyl or C₅-C₈cycloalkyl;         -   R₁₆ is unsubstituted C₁-C₁₈alkyl; C₁-C₁₈alkyl substituted by             hydroxyl, C₁-C₁₂alkoxy, halogen, C₃-C₈cycloalkyl and/or             N(R₈)(R₉); unsubstituted phenyl; phenyl substituted by             C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, hydroxyl and/or             N(R₈)(R₉); or C₅-C₈cycloalkyl; or     -   A if s is more than 1, is a radical of the formula III in which         n is the number s;         -   n is a number from 1 to 1000 or from 0.1 to 1000 if the             siloxane starting material is a mixture of oligomeric             siloxanes,         -   m is a number from 0 to 100;         -   p is a number 0-10 000; and     -   Y is a divalent group C₃-C₁₂cycloalkylene,         C₆-C₁₂bicycloalkylene; C₁-C₆alkylene-C₃-C₁₂cycloalkylene,         C₁-C₆alkylene-C₆-C₁₂bicycloalkylene or C₁-C₁₀alkylene         interrupted by one or more non-consecutive C₃-C₁₂cycloalkyIene,         -U-C₃-C₁₂cycloalkylene, C₆-C₁₂bicycloalkylene or         -U-C₆-C₁₂bicycloalkylene; C₁-C₁₀alkylene interrupted by one or         more non-consecutive O and C₃-C₁₂cycloalkylene,         -U-C₃-C₁₂cycloalkylene, C₆-C₁₂bicycloalkylene and/or         -U-C₆-C₁₂bicycloalkylene;     -   U is U′ or U″     -   U′ is —(CH₂)_(a)COO—;     -   U″ is —Si(CH₃)(CH₃)— or —(CH₂)_(a)—Si(CH₃)(CH₃)—,         -   a is a number from 1 to 10;         -   b is a number from 0 to 10; with the proviso that they are,             however, at least 1 if the methylene group in question is             between two oxygen atoms.

Definitions

C₁-C₁₈Alkyl is linear or branched and is for example C₁-C₁₂-, C₁-C₈-, C₁-C₆- or C₁-C₄alkyl. Examples are methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, iso-butyl, tert-butyl, pentyl, hexyl, heptyl, 2,4,4-trimethyl-pentyl, 2-ethylhexyl, octyl, nonyl, decyl, undecyl, dodecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl or octadecyl.

C₁-C₁₂Alkyl, C₁-C₈alkyl and C₁-C₄alkyI have the same definitions as indicated above but with the corresponding number of carbon atoms.

C₆-C₃₀Alkyl is likewise linear and branched and is for example C₆-C₂₄-, C₆-C₁₂-, C₁₀-C₃₀-, C₁₀-C₂₄-, C₁₂-C₃₀alkyl. Examples are hexyl, heptyl, 2,4,4-:trimethylpentyl, 2-ethylhexyl, octyl, nonyl, decyl, undecyl, dodecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, nonadecyl, icosyl, henicosyl, docosyl, tricosyl, tetracosyl, pentacosyl, hexacosyl, heptacosyl, octacosyl or triacontyl.

C₂-C₁₂Alkyl interrupted by one or more oxygen atoms is for example interrupted 1-9, 1-7 or 1 or 2 times by —O—. Where the radicals are interrupted by two or more —O—, the oxygen atoms are each separate from one another by at least one methylene group. This results, for example, in structural units such as —CH₂—O—CH₃, —CH₂CH₂—O—CH₂CH₃, —[CH₂CH₂O]_(y)—CH₃, where y=1-9, —(CH₂CH₂O)₇CH₂CH₃, —CH₂—CH(CH₃)—O—CH₂—CH₂CH₃ or —CH₂—CH(CH₃)—O—CH₂CH₃.

C₂-C₆Hydroxyalkyl is C₂-C₆alkyl substituted by OH. The alkyl radical is linear or branched and may have the definitions indicated above (with the corresponding number of carbon atoms).

C₂-C6Aminoalkyl is C₂-C₆alkyl substituted by NH₂. The alkyl radical is linear or branched and may have the definitions indicated above (with the corresponding number of carbon atoms).

C₁-C₁₂Alkoxy stands for linear or branched radicals and is for example C₁-C₁₀-, C₁-C₈-, C₁-C₆- or C₁-C₄alkoxy. Examples are methoxy, ethoxy, propoxy, isopropoxy, n-butyloxy, sec-butyloxy, iso-butyloxy, tert-butyloxy, pentyloxy, hexyloxy, heptyloxy, 2,4,4-trimethylpentyloxy, 2-ethylhexyloxy, octyloxy, nonyloxy, decyloxy or dodecyloxy, especially methoxy, ethoxy, propoxy, isopropoxy, n-butyloxy, sec-butyloxy, iso-butyloxy, tert-butyloxy, preferably methoxy. C₁-C₄Alkoxy is likewise linear or branched and has, for example, the definitions indicated above with the corresponding number of carbon atoms.

C₃-C₈-Cycloalkyl is linear or branched alkyl containing at least one ring, for example cyclopropyl, cyclopentyl, methyl-cyclopentyl, cyclohexyl, methyl- or dimethyl-cyclohexyl, or cyclooctyl, especially cyclopentyl and cyclohexyl.

C₅-C₈Cycloalkyl has the definitions indicated above with the corresponding number of carbon atoms.

C₃-C₆Alkenyl may be mono- or polyunsaturated and may be linear or branched and is for example C₃-C₄alkenyl. Examples are allyl, methallyl, 1,1-dimethylallyl, 1-butenyl, 2-butenyl, 1,3-pentadienyl or 1 -hexenyl, especially allyl.

Halogen is fluorine, chlorine, bromine and iodine.

Substituted phenyl is substituted from one to five times, for example once, twice or three times, especially once or twice, on the phenyl ring.

A heterocyclic radical in this context includes not only aliphatic but also aromatic rings containing one or more, especially one or two, heteroatoms. Fused ring systems are included. Examples of suitable heteroatoms include particularly O, N or S. Examples are furyl, thienyl, pyrrolyt, oxinyl, dioxinyl or pyridyl. 5- or 6-membered rings are preferred. As a heterocyclic radical R is for example pyrrolyl, pyrrolidinyl, oxazolyl, pyridinyl, 1,3-diazinyl, 1,2-diazinyl, piperidinyl, morpholinyl, thianthrenyl, furanyl, pyranyl, xanthenyl,. imidazolyl thiazoylyl, pyrimidinyl, indazolinyl, indolyl, indazolyl, purinyl, isoquinolyl, quinolyl, xanthyl, thioxanthyl, acridinyl etc.

Where OR₆-, SR₇- or NR₈R₉-substituted naphthyl, anthracyl, phenanthryl or heterocyclic rings form 5- or 6-membered rings via the radicals R₆, R₇, R₈ and/or R₉ with further substituents on the naphthyl, anthracyl or phenanthryl ring or on the heterocycle or with one of the carbon atoms of the naphthyl, anthracyl or phenanthryl ring or with one of the carbon atoms of the heterocycle, this embraces for example the following structures

in which the arc and the two double bonds are the aromatic ring system in question.

Where R₁, R₂, R₃, R₄ or R₅ as OR₆, SR₇ or NR₈R₉ form a 5- or 6-membered ring with further substituents on the phenyl ring or with a carbon atom of the phenyl ring, this includes for exarnple the following systems:

Where R₈ and R₉, together with the nitrogen atom to which they are attached, form a 5- or 6-membered ring which may also be interrupted by —O— or —NR₁₂-, the rings in question are, for example, saturated or unsaturated rings, examples being aziridine, piperazine, pyrrole, pyrrolidine, oxazole, pyridine, 1,3-diazine, 1,2-diazine, piperidine or morpholine; in particular, morpholinyl, piperidinyl or piperazinyl rings are formed.

The units of the formulae IIIa, IIIb and/or IIIc are arranged randomly or in blocks; i.e. the sequence of these units in the depiction of the formula III is arbitrary. For example, blocks of units of the formula IIIa, IIIb, IIIc may follow one another, but it is also possible for the individual units to be linked in a randomly distributed fashion, depending on the siloxane. used for the preparation.

Alkylene and cycloalkylene groups are divalent forms of alkyl and cycloalkyl group as defined above. C₃-C₁₂Cycloalkylene is preferably cyclopropylene, cyclobutylene, cyclo-pentylene, cyclohexylene.

C₆-C₁₂Bicycloalkylene is preferably bicycloheptylene or bicyclooctylene.

C₁-C₆alkylene-C₃-C₁₂cycloalkylene is for example methylcyclohexylene.

C₁-C₆alkylene-C₆-C₁₂bicycloalkylene is for example bicycloheptylenyl-ethyl.

Preferred Compounds

R in particular is a radical of the formula II or is naphthyl, and is preferably a radical of the formula II.

R₁, R₂, R₃, R₄ and R₅ are especially hydrogen, C₁-C₄alkyl or C₁-C₄alkoxy. Preferably all of R₁-R₅ are hydrogen.

R₆ and R₇ are especially hydrogen, C₁-C₄alkyl; unsubstituted phenyl or phenyl substituted by C₁-C₄alkyl- and/or C₁-C₄alkoxy, or —O-interrupted C₂-C₈alkyl, preferably C₁-C₄alkyl or hydrogen.

R₈ and R₉ are especially C₁-C₄alkyl, preferably methyl, or together with the nitrogen atom to which they are attached form a morpholinyl radical.

R₁₀ is especially C₁-C₄alkyl or phenyl.

R₁₁ is preferably C₁-C₄alkyl or phenyt.

R₁₂ is preferably hydrogen, C₁-C₄alkyl or OH-substituted C₁-C₄alkyl.

R₁₃, R₁₄, R₁₅, R₁₆, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁ and R₂₂ are independently of one another are C₁-C₄alkyl or phenyl, especially methyl.

Y is preferably C₁-C₆alkylene-C₃-C₁₂cycloalkylene, C₁-C₆alkylene-C₆-C₁₂bicycloalkylene, more preferably C₁-C₆alkylene-bicycloheptylenyl; or a group selected from

The group Y is especially preferred a group selected from

If the siloxane starting material is a mixture of oligomeric siloxanes, “n” can also be less than 1 but greater than 0. In this case it is for example a number between 0.1 and 1000; 0.5 and 1000; 0.8 and 1000 etc.

“a” is preferably a number from 1 to 10, especially 1-3;

“b” is preferably a number from 0 to 10, especially 1-3;

“n” is preferably from 1 to 100 or from 0.1 to 100; especially 1-10;

“p” is preferably 1 to 100, for example from 1 to 50 or from 1 to 25; and

“m” is preferably 0 to 10, especially 0.

“s” is preferably a number from 1-10, especially 1 or 2.

Preference is thus given to compounds of formula I, wherein

R is naphthyl or a radical of the formula II in which

R₁, R₂, R₃, R₄ and R₅ independently of one another are hydrogen, C₁-C₄alkyl or C₁-C₄alkoxy;

s is a number from 1-10,

A if s is 1, is a surface-active radical of the formula III in which G₁ and G₂ have the definition indicated above, and R₁₃, R₁₄, R₁₅, R₁₆, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁ and R₂₂ independently of one another are C₁-C₄alkyl or phenyl,

A if s is more than 1 Is a radical of the formula III in which n is s;

n is a number from 1 to 10 or from 0.1 to 10, if the siloxane starting material is a mixture of oligomeric siloxanes;

m is a number from 0 to 10;

p is a number 0-100;

Y is C₁-C₆alkylene-C₃-C₁₂cycloalkylene, C₁-C₆alkylene-C₆-C₁₂bicycloalkylene; or a group selected from

a is a number from 1 to 3; b is a number from 0 to 3; with the proviso that they are, however, at least 1 if the methylene group in question is between two oxygen atoms.

Particular preference is given to compounds of formula I, wherein

R is phenyl,

s is 1 or 2;

A if s is 1, is a surface-active radical of the formula III in which G₁ and G₂ have the definition indicated above and R₁₃, R₁₄, R₁₅, R₁₆, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁ and R₂₂ are methyl;

A if s is 2 is a radical of the formula III in which n is 2;

n is a number from 1 to 10 or 0.1 to 10 if the siloxane starting material is a mixture of oligomeric siloxanes;

m is 0;

p is a number 0-100;

Y is C₁-C₆alkylene-bicycloheptylenyl, or a group selected from

and a is a number from 1 to 3; b is a number from 0 to 3; with the proviso that they are, however, at least 1 if the methylene group in question is between two oxygen atoms.

Preparation of the Compounds of Formula I

The compounds of the formula I are prepared by customary methods known to the person skilled in the art.

I, Starting with an alkenyl-modified siloxane compound:

wherein R,Y, U′, G₁ and R₁₃ are as defined above, Y″ together with —CH═CH₂ is a divalent group C₃-Cl₂cycloalkenylene, C₆-C₁₂bicyclo-alkenylene; or C₁-C₆alkylene-C₃-C₁₂cycloalkenylene or C₁-C₆alkylene-C₆-C₁₂bicyclo-alkenylene, or is Cl-Cloalkylene interrupted by one or more non-consecutive C₃-Cl₂cycloalkylene, -U-C₃-C₁₂cycloalkylene, C₆-C₁₂bicycloalkylene or -U-C₆-C₁₂bicycloalkylene; C₁-C₁₀alkylene interrupted by one or more non-consecutive O and C₃-C₁₂cycloalkylene, -U-C₃-C₁₂cycloalkylene, C₆-C₁₂bicycloalkylene and/or --U-C₆-C₁₂bicycloalkylene.

The double bound of the alkenyl-moiety on the siloxane reagent can also be the double bound of a cycloalkenyl residue or of a bicycloalkenyl residue.

For example, the group (Y″-CH═CH₂) is norbornenyl or norbornenylethyl resulting in a group Y being bicycloheptylene or bicycloheptylenylethyl.

l “. . . ” means that the radical of the siloxane molecule moiety defined in formula III adjoins this site (in accordance with formula III, in this reaction m must be 0 in the starting material).

The reaction temperatures are appropriately held within a range of 20-150° C., preferably 60-110° C. Moreover, it is appropriate to carry out the reaction, for example, in a suitable aprotic organic solvent, such as tetrahydrofuran (THF), dioxane, hexane, heptane, cyclohexane, toluene, xylene, benzene or chlorobenzene, or in a suitable protic solvent such as water. It is also possible, however, to operate without solvents, for example.

The reaction mixture is normally stirred while the reaction is carried out.

It is also appropriate to carry out the reaction under inert conditions, for example under an argon or nitrogen atmosphere.

Examples of catalysts appropriate for carrying out the reaction are noble metal catalysts, such as palladium or palladium complexes. Such reactions are described for examples by Hosokawa et al. in Chem. Lett. (1989) 2001, by Bergbreiter et al. in J. Org. Chem. (1989) 54 (11) 2726 or by Trost et al. in J. Am. Chem. Soc. (1985) 107 (21) 6123.

Furthermore the reaction may be carried out using an acid as catalyst, for example H₂SO₄.

Examples of reaction performed in an acidic milieu (H₂SO₄) are given by Kirchanov et al. in lzv. Akad. Nauk. SSSR, Ser. Khim. (1981) (6)1914.

II, Starting with an alkenyl-modified siloxane compound:

wherein R,Y, U″, G₁ and R₁₃ are as defined above, Y″ together with —CH═CH₂ is a divalent group C₃-C₁₂cycloalkenylene, C₆-C₁₂bicyclo-alkenylene; or C₁-C₆alkylene-C₃-C₁₂cycloalkenylene or C₁-C₆alkylene-C₆-C₁₂bicyclo-alkenylene, or is C₁-C₁₀alkylene interrupted by one or more non-consecutive C₃-C₁₂cycloalkylene, -U-C₃-C₁₂cycloalkylene, C₆-C₁₂bicycloalkylene or U-C₆-C₁₂bicycloalkylene; C₁-C₁₀alkylene interrupted by one or more non-consecutive O and C₃-C₁₂cycloalkylene, -U-C₃-C₁₂cycloalkylene, C₆-C₁₂bicycloalkylene and/or -U-C₆-C₁₂bicycloalkylene. The double bound of the alkenyl-moiety on the siloxane reagent can also be the double bound of a cycloalkenyl residue or of a bicycloalkenyl residue. For example, the group (Y″-CH═CH₂) is norbornenyl or norbornenylethyl resulting in a group Y being bicycloheptylene or bicycloheptylenylethyl.

; “. . . ” means that the radical of the siloxane molecule moiety defined in formula III adjoins this site (in accordance with formula III, in this reaction m must be 0 in the starting material).

The reaction temperatures are appropriately held within a range of 20-150° C., preferably 60-110° C. Moreover, it is appropriate to carry out the reaction, for example, in a suitable aprotic organic solvent, such as tetrahydrofuran (THF), dioxane, hexane, heptane, cyclohexane, toluene, xylene, benzene or chlorobenzene. It is also possible, however, to operate without solvents, for example.

The reaction mixture is normally stirred while the reaction is carried out.

It is also appropriate to carry out the reaction under inert conditions, for example under an argon or nitrogen atmosphere.

Examples of catalysts appropriate for carrying out the reaction are noble metal catalysts, such as platinum or rhodium catalysts. Examples of platinum catalysts are H₂PtCl₆ or PtCl₂(C₆H₅—CH═CH₂)₂. These catalysts may also, for example, have been applied to suitable support materials, such as alumina, such as Pt/Al₂O₃ (for example, available from Heraeus). Carbon, for example, may also be used as a support material (Pt/C—which catalyst need not be anhydrous—available, for example, from Johnson Matthey). Examples of suitable catalysts are platinum, palladium, rhodium,. nickel, cobalt or other metals, especially as powders or in the form of complexes. Examples are platinum sponge, platinum black, chloroplatinic acid, the reaction product of chloroplatinic acid and alcohol, and a complex of chloroplatinic acid and vinylsiloxane.

Catalysts of this kind are available commercially, e.g. platinum carbonyl-cyclovinylmethyl-siloxane complex, platinum.-divinyltetramethyldisiloxane complex, platinum-octyl aldehyde/octanol complex, or may be obtained by methods customary in the art and known to the person skilled in the art.

The concentration of the catalyst is appropriately for example 1-1 000 ppm, e.g. 150-400 ppm.

Bicyclalkylene substituted siloxanes as for example α-ωbis(norbornenyl)dimethylpolysiloxanes may be prepared as described in DE 4128932 or α-ωbis(2(norbornenyl)ethyi)dimethylpolysiloxanes as described by U. Mueller at al. in J. Macromol. Sci., Pure Appl. Chem. (1996) A33(4) 439-57.

III. The compounds of the formula I in which A is a surface-active siloxane radical of the formula III may also be prepared by reacting the corresponding glyoxalic acid with a siloxane having a siloxane having epoxide radicals:

The reaction proceeds in the presence of an acid or of a base.

R, G₁, U′ and R₁₃ have the definition indicated above.

R′ is C₁-C₁₀alkylene, C₁-C₁₀alkylene interrupted by O;

R″ is C₃-C₁₂cycloalkylene, C₆-C₁₂bicycloalkylene, C₁-C₆alkylene-C₃-C₁₂cycloalkylene or C₁-C₆alkylene-C₆-C₁₂bicycloalkylene.

“. . . ” means that the radical of the siloxane molecule defined in formula III adjoins this site.

Siloxanes having an epoxygroup are described in DE 4128894.

Some of the siloxane compounds are available commercially, or they may be obtained by methods known to the person skilled in the art. For example, methods of preparation and/or literature citations for the preparation can be found in the Geleste catalogue “ABCR Geleste 2000”, pages 434-447.

The preparation of the starting materials required for the synthesis of the compounds of the formula I of the invention is common knowledge and is well known to the person skilled in the art. Indeed, some of the compounds are available commercially.

For example the aryglyoxalic acid Is commercially available.

The preparation of the alcohols is well known to the person skilled in the art and is widely described in the literature. Many of these compounds are available commercially.

The invention also provides novel compounds of the formula I.

Compositions

The invention also provides photopolymerizable compositions comprising

(A) at least one ethylenically unsaturated free-radically photopolymerizable compound; and

(B) at least one surface-active photoinitiator of the formula I.

The invention further provides photopolymerizable compositions comprising

(A) at least one ethylenically unsaturated free-radically photopolymerizable compound;

(B) at least one surface-active photoinitiator of the formula I, and

(C) at least one thermally crosslinkable compound and optionally comprising in addition to components (A) and (B) or (A), (B) and (C) further additives (D) and/or additional photoinitiators (E).

Definition of the Composition Components

The unsaturated compounds (A) may contain one or more olefinic double bonds. They may be of low (monomeric) or relatively high (oligomeric) molecular mass. Examples of monomers containing a double bond are alkyl or hydroxyalkyl acrylates or methacrylates, such as methyl, ethyl, butyl, 2-ethylhexyl or 2-hydroxyethyl acrylate, isobornyl acrylate, methyl methacrylate or ethyl methacrylate. Other examples are acrylnitrile, acrylamide, methacrylamide, N-substituted (meth)acrylamides, vinyl esters such as vinyl acetate, vinyl ethers such as isobutyl vinyl ether, styrene, alkylstyrenes and halostyrenes, N-vinylpyrrolidone, vinyl chloride or vinylidene chloride.

Examples of monomers containing two or more double bonds are ethylene glycol, propylene glycol, neopentyl glycol, hexamethylene glycol and bisphenol A diacrylates, 4,4′-bis(2-acryl-oyloxyethoxy)diphenylpropane, trimethylolpropane triacrylate, pentaerythritol triacrylate or tetraacrylate, vinyl acrylate, divinylbenzene, divinyl succinate, diallyl phthalate, triallyl phosphate, triallyl isocyanurate or tris(2-acryloylethyl) isocyanurate.

Examples of relatively high molecular mass (oligomeric) polyunsaturated compounds are acrylated epoxy resin and acrylated or vinyl ether- or epoxy-functional polyesters, polyurethanes and polyethers. Further examples of unsaturated oligomers are unsaturated polyester resins, generally prepared from maleic acid, phthalic acid and one or more diols and having molecular weights of from about 500 to 3000. In addition to these it is also possible to use vinyl ether monomers and oligomers, and also maleate-terminated oligomers with polyesters, polyurethane, polyether, polyvinyl ether and epoxide main chains. Especially suitable are combinations of polymers and oligomers which carry vinyl ether groups, as described in WO 90/01512. Also suitable, however, are copolymers of monomers functionalized with maleic acid and vinyl ether.

Also suitable are compounds containing one or more free-radically polymerizable double bonds. In these compounds the free-radically polymerizable double bonds are preferably in the form of (meth)acryloyl groups. (Meth)acryloyl and, respectively, (meth)acrylic here and below means acryloyl and/or methacryloyl, and acrylic and/or methacrylic, respectively. Preferably, at least two polymerizable double bonds are present in the molecule in the form of (meth)acryloyl groups. The compounds in question may comprise, for example, (meth)acryloyl-functional oligomeric and/or polymeric compounds of poly(meth) acrylate. The number-average molecular mass of this compound may be for example from 300 to 10 000, preferably from 800 to 10 000. The compounds preferably containing free-radically polymerizable double bonds in the form of (meth)acryloyl groups may be obtained by customary methods, for example by reacting poly(meth)acrylates with (meth)acrylic acid. These and other preparation methods are described in the literature and are known to the person skilled in the art.

Unsaturated oligomers of this kind may also be referred to as prepolymers.

Functionalized acrylates are also suitable. Examples of suitable monomers which are normally used to form the backbone (the base polymer) of such functionalized acrylate and methacrylate polymers are acrylate, methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, n-butyl acrylate, n-butyl methacrylate, isobutyl acrylate, isobutyl methacrylate, 2-ethylhexyl acrylate, 2-ethylhexyl methacrylate etc. Additionally, appropriate amounts of functional monomers are copolymerized during the polymerization in order to give the functional polymers. Acid-functionalized acrylate or methacrylate polymers are obtained using acid-functional monomers such as acrylic acid and methacrylic acid. Hydroxy-functional acrylate or methacrylate polymers are formed from hydroxy-functional monomers, such as 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate and 3,4-dihydroxybutyl methacrylate. Epoxy-functionalized acrylate or methacrylate polymers are obtained using epoxy-functional monomers such as glycidyl methacrylate, 2,3-epoxybutyl methacrylate, 3,4-epoxybutyl methacrylate, 2,3-epoxycyclohexyl methacrylate, 10,11-epoxyundecyl methacrylate etc. Similarly, for examle, isocyanate-functionalized polymers may be prepared from isocyanate-functionalized monomers, such as meta-isopropenyl-α,α-dimethylbenzyl isocyanate, for example.

Particularly suitable compounds are, for example, esters of ethylenically unsaturated monofunctional or polyfunctional carboxylic acids and polyols or polyepoxides, and polymers containing ethylenically unsaturated groups in the chain or in side groups, such as unsaturated polyesters, polyamides and polyurethanes and copolymers thereof, alkyd resins, polybutadiene and butadiene copolymers, polyisoprene and isoprene copolymers, polymers and copolymers containing (meth)acrylic groups in side chains, and also mixtures of one or more such polymers.

Examples of suitable monofunctional or polyfunctional unsaturated carboxylic acids are acrylic acid, methacrylic acid, crotonic acid, itaconic acid, cinnamic acid, maleic acid, fumaric acid, unsaturated fatty acids such as linolenic acid or oleic acid. Acrylic acid and methacrylic acid are preferred.

It is, however, also possible to use saturated dicarboxylic or polycarboxylic acids- in a mixture with unsaturated carboxylic acids. Examples of suitable saturated dicarboxylic or polycarboxylic acids include tetrachlorophthalic acid, tetrabrqmophthalic acid, phthalic acid, trimellitic acid, heptanedicarboxylic acid, sebacic acid, dodecanedicarboxylic acid, hexahydrophthalic acid, etc.

Suitable polyols include aromatic and especially aliphatic and cycloaliphatic polyols. Examples of aromatic polyols are hydroquinone, 4,4′-dihydroxybiphenyl, 2,2-di(4-hydroxy-phenyl)propane, and also novolaks and resols. Examples of polyepoxides are those based on the aforementioned polyols, especially the aromatic polyols, and epichlorhydrin. Further suitable polyols include polymers and copolymers containing hydroxyl groups in the polymer chain or in side groups, such as polyvinyl alcohol and copolymers thereof or polyhydroxyalkyl methacrylates or copolymers thereof, for example. Oligoesters containing hydroxyl end groups are further suitable polyols.

Examples of aliphatic and cycloaliphatic polyols are alkylenediols having preferably from 2 to 12 carbon atoms, such as ethylene glycol, 1,2- or 1,3-propanediol, 1,2-, 1,3- or 1,4-butanediol, pentanediol, hexanediol, octanediol, dodecanediol, diethylene glycol, triethylene glycol, polyethylene glycols having molecular weights of preferably from 200 to 1500, 1 ,3-cyclopentanediol, 1,2-, 1,3- or 1,4-cyclohexanediol, 1,4-dihydroxymethylcyclohexane, glycerol, tris(P-hydroxyethyl)amine, trimethylolethane, trimethylolpropane, pentaerythritol, dipentaerythritol and sorbitol.

The polyols may have been partly or fully esterified with one or more different unsaturated carboxylic acids, the free hydroxyl groups in partial esters possibly having been modified, e.g. etherified or esterified with other carboxylic acids.

Examples of esters are: trimethylolpropane triacrylate, trimethylolethane triacrylate, trimethylolpropane trimethacrylate, trimethylolethane trimethacrylate, tetramethylene glycol dimethacrylate, triethylene glycol dimethacrylate, tetraethylene glycol diacrylate, pentaerythritol diacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, dipentaerythritol diacrylate, dipentaerythritol triacrylate, dipentaerythritol tetraacrylate, dipentaerythritol pentaacrylate, dipentaerythritol hexaacrylate, tripentaerythritol octaacryiate, pentaerythritol dimethacrylate, pentaerythritol trimethacrylate, dipentaerythritol dimethacrylate, dipentaerythritol tetramethacrylate, tripentaerythritol octamethacrylate, pentaerythritol diitaconate, dipentaerythritol trisitaconate, dipentaerythritol pentaitaconate, dipentaerythritol hexaitaconate, ethylene glycol diacrylate, 1,3-butanediol diacrylate, 1,3-butanediol dimethacrylate, 1,4-butanediol diitaconate, sorbitol triacrylate, sorbitol tetraacrylate, modified pentaerythritol triacrylate, sorbitol tetramethacrylate, sorbitol pentaacrylate, sorbitol hexaacrylate, oligoester acrylates and methacrylates, glycerol diacrylate and triacrylate, 1,4-cyclohexane diacrylate, bisacrylates and bismethacrylates of polyethylene glycol having a molecular weight from 200 to 1500, or mixtures thereof.

Suitable components (A) also include the amides of identical or different unsaturated carboxylic acids with aromatic, cycloaliphatic andaliphatic polyamines having preferably from 2 to 6, particularly from 2 to 4 amino groups. Examples of such polyamines are ethylenediamine, 1,2- or 1,3-propylenediamine, 1,2-, 1,3- or 1,4-butylenediamine, 1,5-pentylenediamine, 1,6-hexylenediamine, octylenediamine, dodecylenediamine, 1,4-diaminocyclohexane, isophoronediamine, phenylenediamine, bisphenylenediamine, di-β-aminoethyl ether, diethylenetriamine, triethylenetetramine, di(β-aminoethoxy)- or di(β-aminopropoxy)ethane. Further suitable polyamines are polymers and copolymers containing possibly additional amino groups in the side chain, and oligoamides having amino end groups. Examples of such unsaturated amides are: methylenebisacrylamide, 1 ,6-hexamethylenebisacrylamide, diethylenetriaminetrismethacrylamide, bis(methacrylamidopropoxy)ethane, β-methacrylamidoethyl methacrylate, and N-[(β-hydroxyethoxy)ethyl]-acrylamide.

Suitable unsaturated polyesters and polyamides are derived, for example, from maleic acid and diols or diamines. The maleic acid may have been replaced in part by other dicarboxylic acids. They may be used together with ethylenically unsaturated comonomers, e.g. styrene. The polyesters and polyamides may also be derived from dicarboxylic acids and ethylenically unsaturated diols or diamines, especially from relatively long chain ones having, for example, from 6 to 20 carbon atoms. Examples of polyurethanes are those synthesized from saturated or unsaturated diisocyanates and unsaturated or saturated diols, respectively.

Polybutadiene and polyisoprene and copolymers thereof are known. Examples of suitable comonomers are olefins such as ethylene, propene, butene, hexene, (meth)acrylates, acrylonitrile, styrene or vinyl chloride. Polymers containg (meth)acrylate groups in the side chain are likewise known. They may comprise, for example, reaction products of novolak-based epoxy resins with (meth)acrylic acid, homopolymers or copolymers of vinyl alcohol or the hydroxyalkyl derivatives thereof that have been estedfied with (meth)acrylic acid, or homopolymers and copolymers of (meth)acrylates esterified with hydroxyalkyl (meth)acrylates.

The photopolymerizable compounds (A) may be used alone or in any desired mixtures. Preference is given to using mixtures of polyol (meth)acrylates.

It is also possible to add binders to the compositions of the invention, which is especially appropriate when the photopolymerizable compounds are liquid or viscous substances. The amount of the binder can be for example 5-95, preferably 10-90 and especially 40-90% by weight, based on the overall. solids. The choice of binder is made depending on the field of use and the properties required for that field, such as developability in aqueous and organic solvent systems, adhesion to substrates, and oxygen sensitivity, for example.

Examples of suitable binders are polymers having a molecular weight of approximately 5 000-2 000 000, preferably 10 000-1 000 000. Examples are: homopolymeric and copolymeric acrylates and methacrylates, e.g. copolymers of methyl methacrylate/ethyl acrylate/methacrylic acid, poly(alkyl methacrylates), poly(alkyl acrylates); cellulose esters and cellulose ethers such as cellulose acetate, cellulose acetate butyrate, methylcellulose, ethylcellulose; polyvinylbutyral, polyvinylformal, cyclized rubber, polyethers such as polyethylene oxide, polypropylene oxide, polytetrahydrofuran; polystyrene, polycarbonate, polyurethane, chlorinated polyolefins, polyvinyl chloride, copolymers of vinyl chloride/vinylidene chloride, copolymers of vinylidene chloride with acrylonitrile, methyl methacrylate and vinyl acetate, polyvinyl acetate, copoly(ethylene/vinyl acetate), polymers such as polycaprolactam and poly(hexamethyleneadipamide), polyesters such as poly(ethylene glycol terephtalate) and poly(hexamethylene glycol succinate).

As component (A), i.e. UV-curable component, it is also possible to use the resins listed later on below under (C1). Examples of those that are of particular interest are unsaturated acrylates containing reactive functional groups. The reactive functional group may be selected, for example, from a hydroxyl, thiol, isocyanate, epoxide, anhydride, carboxyl, amino or a blocked amino group. Examples of OH-containing unsaturated acrylates are hydroxyethyl and hydroxybutyl acrylates or else glycidyl acrylates.

The unsaturated compounds may also be used in a mixture with non-photopolymenizable film-forming components. These may be, for example, physically drying polymers or their solutions in organic solvents, such as nitrocellulose or cellulose acetobutyrate, for example. They may also, however, be chemically and/or thermally curable resins, such as polyisocyanates, polyepoxides or melamine resins, for example. By melamine resins are meant not only condensates of melamine (1,3,5-triazine-2,4,6-triamine) but also those of melamine derivatives. In general the components comprise a film-forming binder based on a thermoplastic or thermosettable resin, predominantly on a thermosettable resin. Examples thereof are alkyd, acrylic, polyester, phenolic, melamine, epoxy and polyurethane resins and mixtures thereof. The additional use of thermally curable resins is of importance for use in what are known as hybrid systems, which may be both photopolymerized and also thermally crosslinked.

Component (A) may comprise, for example, a coating composition comprising

(A1) compounds containing one or more free-radically polymerizable double bonds and further containing at least one other functional group which is reactive in the sense of an addition reaction and/or condensation reaction (examples have been given above),

(A2) compounds containing one or more free-radically polymerizable double bonds and further containing at least one other functional group which is reactive in a sense of an addition reaction and/or condensation reaction, the additional reactive functional group being complementary to or reactive toward the additional reactive functional groups of component (A1),

(A3) if desired, at least one monomeric, oligomeric and/or polymeric compound containing at least one functional group which is reactive in the sense of an addition reaction and/or condensation reaction toward the functional groups from component (A1) or component (A2) that are present in addition to the free-radically polymerizable double bonds. Component (A2) carries in each case the groups which are reactive toward or complementary to component (A1). ln this context it is possible in each case for different kinds of functional groups to be present in one component. In component (A3) there is a further component available containing functional groups which are reactive in the sense of addition reactions and/or condensation reactions and which are able to react with the functional groups of (A1) or (A2) that are present in addition to the free-radically polymerizable double bonds. Component (A3) contains no free-radically polymerizable double bonds. Examples of such combinations of (A1), (A2), (A3) can be found in WO 99/55785. Examples of suitable reactive functional groups are selected, for example, from hydroxyl, isocyanate, epoxide, anhydride, carboxyl or blocked amino groups. Examples have been described above.

Constituents of component (C) are, for example, thermally curable coating system constituents that are customary in the art. Accordingly, component (C) may comprise two or more constituents.

Examples of component (C) are oligomers and/or polymers derived from α,β-unsaturated acids and derivatives thereof; examples are polyacrylates and polymethacrylates, and polyacrylonitriles, polyacrylamides and polymethyl methacrylates that have been impact-modified using butyl acrylate. Further examples of component (C) are urethanes, polyurethanes derived from polyethers, polyesters and polyacrylates containing free hydroxyl groups or thiol groups, on the one hand, and aliphatic or aromatic polyisocyanates, on the other, and also precursors thereof. Accordingly, component (C) also comprises, for example, crosslinkable acrylic resins derived from substituted acrylates, such as epoxy acrylates, urethane acrylates or polyester acrylates. It is also possible for alkyd resins, polyester resins and acrylic resins and their modifications, which are crosslinked with melamine resins, urea resins, isocyanates, isocyanurates, polyisocyanates, polyisocyanurates and epoxy resins, to be constituents of component (C).

Component (C) generally comprises for example, a film-forming binder based on a thermoplastic or thermosettable resin, predominantly on a thermosettable resin. Examples thereof are alkyd, acrylic, polyester, phenolic, melamine, epoxy and polyurethane resins and mixtures thereof. Examples of these are described, for example, in Ullmann's Encyclopedia of Industrial Chemistry, 5th Ed., Vol. A18, pp. 368-426, VCH, Weinheim 1991.

Component (C) may be a cold-curable or heat-curable binder, and the addition of a curing catalyst may be advantageous. Suitable catalysts that accelerate the curing of the binder are described, for example, in Ullmann's Encyclopedia of Industrial Chemistry, Vol. A18, p.469, VCH Verlagsgesellschaft, Weinheim 1991.

Examples of specific binders suitable as component (C) are

1. Paints based on cold- or heat-crosslinkable alkyd, acrylate, polyester, epoxy or melamine resins or mixtures of such resins, with or without addition of a curing catalyst;

2. Two-component polyurethane paints based on hydroxyl-containing acrylate, polyester or polyether resins and on aliphatic or aromatic isocyanates, isocyanurates or polyisocyanates;

3. One-component polyurethane paints based on blocked isocyanates, isocyanurates or polyisocyanates that are deblocked in the course of stoving; melamine resins can also be added, if appropriate;

4. One-component polyurethane paints based on aliphatic or aromatic urethanes or polyurethanes and on hydroxyl-containing acrylate, polyester or polyether resins;

5. One-component polyurethane paints based on aliphatic or aromatic urethane acrylates or polyurethane acrylates having free amine groups in the urethane structure and on melamine resins or polyether resins, with or without addition of a curing catalyst;

6. Two-component paints based on (poly)ketimines and on aliphatic or aromatic isocyanates, isocyanurates or polyisocyanates;

7. Two-component paints based on (poly)ketimines and on an unsaturated acrylate resin or a polyacetoacetate resin or a methacrylamidoglycolate methyl ester;

8. Two-component paints based on carboxyl- or amino-containing polyacrylates and polyeopoxides;

9. Two-component paints based on acrylate resins containing anhydride groups and on a polyhydroxy or polyamino component;

10. Two-component paints based on acrylate-containing anhydrides and polyepoxides;

11. Two-component paints based on (poly)oxazolines and on acrylate resins containing anhydride groups, or unsaturated acryiate resins or aliphatic or aromatic isocyanates, isocyanurates or polyisocyanates;

12. Two-component paints based on unsaturated polyacrylates and polymalonates;

13. Thermoplastic polyacrylate paints based on thermoplastic acrylate resins or externally crosslinking acrylate resins in combination with etherified melamine resins;

14. Paint systems based on urethane (meth)acrylate containing (meth)acryloyl groups and free isocyanate groups and on one or more isocyanate-reactive compounds, such as unesterified or esterified polyols. Such systems are published, for example, in EP 928800.

Blocked isocyanates as may be employed, inter alia, in component (C) are described, for example, in Organischer Metallschutz: Entwicklung und Anwendung von Beschichtungsstoffen [Organic Protection of Metals: Development and Application of Coating Materials], page 159-160, Vincentz Verlag, Hannover (1993). These are compounds in which the highly reactive NCO group is ‘blocked’ by reaction with specific radicals, such as primary alcohols, phenol, acetoacetates, F-caprolactam, phthalimide, imidazole, oxime or amine. The blocked isocyanate is stable in liquid systems and also in the presence of hydroxyl groups. On heating, the blocking agents are eliminated and the NCO group is exposed.

Both 1-component (1K) and 2-component (2K) systems may be used as component (C). Examples of such systems are described in Ullmann's Encyclopedia of Industrial Chemistry, Vol. A18, Paints and Coatings, page 404-407, VCH Verlagsgesellschaft mbH, Weinheim (1991).

The composition may be optimized by specially adapting the formulation, for example by varying the binder/crosslinker ratio. Such measures are well known to the person skilled in the art of coatings technology.

In the curing process of the invention the component (C) is preferably a mixture based on acrylate/melamine (and melamine derivatives), 2-component polyurethane, 1-component polyurethane, 2-component epoxy/carboxy or 1-component epoxy/carboxy. Mixtures of these. systems are also possible, an example being the addition of melamine (or derivatives thereof) to 1-component polyurethanes.

Component (C) is preferably a binder based on a polyacrylate with melamine or on a melamine derivative. Preference is also given to a system based on a polyacrylate polyol and/or polyester polyol with an unblocked polyisocyanate or polyisocyanurate.

Component (C) may further comprise monomeric and/or oligomeric compounds containing ethylenically unsaturated bonds (prepolymers) which additionally contain at least one or more OH, NH₂, COOH, epoxy or NCO groups (=C1) capable of reaction with the binder and/or crosslinker substituent of component (C). Following application and thermal curing, the ethylenically unsaturated bonds are converted by UV radiation into a crosslinked, high molecular mass form. Examples of such components (C) are described, for example, in the abovementioned publication Ullmann's Encyclopedia of Industrial Chemistry, 5th Ed., Vol. A18, pages 451-453, or by S. Urano, K. Aoki, N. Tsuboniva and R. Mizuguchi in Progress in Organic Coatings, 20 (1992), 471-486, or by H. Terashima and 0. Isozaki in JOCCA 1992 (6), 222.

(C1) may be, for example, an OH-containing unsaturated acrylate, e.g. hydroxyethyl or hydroxybutyl acrylate or else glycidyl acrylates. The component (C1) may be of any desired construction (e.g.. polyester, polyacrylate, polyether, etc., units) provided there are an ethylenically unsaturated double bond and also free OH, COOH, NH₂, epoxy or NCO groups.

(C1) may also be obtained, for example, by reacting an epoxy-functional oligomer with acrylic acid or methacrylic acid. A typical example of an OH-functional oligomer containing vinylic double bonds is

obtained by reacting CH₂═CHCOOH with

One possibility for preparing component (C1) is also, for example, the reaction of an oligomer that contains only one epoxy group and at another site in the molecule possesses a free OH group.

The ratio of components (A) to.(C) in the UV-crosslinking and thermally crosslinking formulations is not critical. “Dual-cure” systems are well known to the person skilled in the art, who is therefore well aware of the optimum proportions of the UV-crosslinkable and thermally crosslinkable components for the particular desired application. For example, the compositions may comprise components (A) and (C) in a ratio of from 5:95 to 95:5, from 20:80 to 80:20 or from 30:70 to 70:30, e.g. from 40:60 to 60:40.

Examples of “dual-cure” systems, i.e. systems containing both UV-curable and thermally curable components, may be. found, inter alia, in U.S. Pat. No. 5,922,473, columns 6 to 10.

Besides the photoinitiator, the photopolymerizable mixtures may comprise further additives (D). Examples of these are thermal inhibitors, which are intended to prevent premature polymerization, such as hydroquinone, hydroquinone derivatives, p-methoxyphenol, β-naphthol or sterically hindered phenois such as 2,6-di(tert-butyl)-p-cresol. To increase the dark storage stability it is possible to use copper compounds, such as copper naphthenate, copper stearate or copper octoate, phosphorus compounds, such as triphenylphosphine, tributylphosphine, triethyl phdsphite, triphenyl phosphite or tribenzyl phosphite, quaternary ammonium compounds, such as tetramethylammonium chloride or trimethylbenzylammonium chloride, or hydroxylamine derivatives, such as N-diethylhydroxylamine, for example. For the purpose of excluding atmospheric oxygen in the course of the polymerization it is possible to add paraffin or similar wax-like substances, which at the beginning of polymerization migrate to the surface, on account of their poor solubility in the polymer, where they form a transparent surface layer which prevents the ingress of air. Similarly, it is possible to apply an oxygen-impermeable layer. Light stabilizers which can be added include UV absorbers, such as those of the hydroxyphenylbenzotriazole, hydroxyphenylbenzo- phenone, oxalmide or hydroxyphenyl-s-triazine type. These compounds may be used individually or in mixtures, with or without the use of sterically hindered amines (HALS).

The photopolymerization may further be accelerated by adding photosensitizers as further additives (D), which shift or broaden the spectral sensitivity. These photosensitizers are, in particular, aromatic carbonyl compounds such as benzophenone derivatives, thioxanthone derivatives, and also especially isopropylthioxanthone, anthraquinone derivatives and 3-acylcoumarin derivatives, terphenyls, styryl ketones, and also 3-(aroylmethylene)-thiazolines, camphorquinone, and also eosine dyes, rhodamine dyes and erythrosine dyes.

In order to accelerate the photopolymerization it is possible. to add, as further additives (D), amines, such as triethanolamine, N-methyidiethanolamine, ethyl p-dimethylaminobenzoate, or Michler's ketone. The effect of the amines may be boosted by adding aromatic ketones of the benzophenone type. Examples of amines which can be used as oxygen scavengers are substituted N,N-dialkylanilines, as described in EP-A 339841. Further accelerators, coinitiators and autoxidizers are thiols, thioethers, disulfides and phosphines, as described for example in EP 438123 and GB 2180358.

It is also possible to add chain transfer reagents customary in the art to the compositions of the invention. Examples are mercaptans, amines and benzothiazole.

The curing process, especially of compositions which are pigmented (with titanium dioxide for example), may also be assisted by adding an additional additive (D) which is a component which under thermal conditions forms free radicals, such as an azo compound, for instance 2,2′-azobis(4-methoxy-2,4-dimethylvaleronitrile), a triazene, diazo sulfide, pentazadiene or a peroxy compound such as hydroperoxide or peroxycarbonate, e.g. t-butyl hydroperoxide, as described for example in EP 245639.

As further additives (D), the compositions may also comprise, for example, a photoreducible dye, such as xanthene, benzoxanthene, benzothioxanthene, thiazine, pyronine, porphyrin or acridine dyes, and/or a radiation-cleavable trihalomethyl compound. Similar compositions are described, for example, in EP 445624.

Further common additives (D) - depending on the intended use - include optical brighteners, fillers, e.g. kaolin, talc, barytes, gypsum, chalk or silicatic fillers, pigments, dyes, wetting agents or flow improvers.

For the curing of thick and pigmented coatings it is appropriate to add glass microbeads or pulverized glass fibres, as described for example in U.S. Pat. No. 5,013,768.

The formulations may also comprise dyes and/or white or coloured pigments. Depending on the intended application, both organic and inorganic pigments may be used. Such additions are known to the person skilled in the art; some examples are titanium dioxide pigments, of, for example, the rutile or anatase type, carbon black, zinc oxide, such as zinc white, iron oxides, such as yellow iron oxide, red iron oxide, chrome yellow, chrome green, nickel titanium yellow, ultramarine blue, cobalt blue, bismuth vanadate, cadmium yellow or cadmium red. Examples of organic pigments are monoazo or disazo pigments, and also metal complexes thereof, phthalocyanine pigments, polycyclic pigments, such as perylene, anthraquinone, thioindigo, quinacridone or triphenylmethane pigments, and also diketopyrrolopyrrole, isoindolinone, e.g. tetrachloroisoindolinone, isoindoiine, dioxazine, benzimidazolone and quinophthalone pigments.

The pigments may be used individually or else in a mixture in the formulations.

The pigments, depending on the intended use, are added to the formulations in the amounts customary in the art, for example in an amount of from 1 to 60% by weight, or from 10 to 30% by weight, based on the overall mass.

The formulations may also, for example, comprise organic dyes from a very wide variety of classes. Examples are azo dyes, methine dyes, anthraquinone dyes or metal complex dyes. Customary concentrations are, for example, from 0.1 to 20%, in particular from 1 to 5%, based on the overall mass.

The choice of additives is guided by the respective field of application and by the properties desired for this field. The above-described additives (D) are customary in the art and, accordingly, are used in the amounts that are customary in the art.

Where the photoinitiators of the invention are employed in hybrid systems, i.e. systems which can be cured both free-radically and cationically, use is made, in addition to the free-radical curing agents of the formula I and any further free-radical curing agents, of cationic photoinitiators such as benzoyl peroxide (other suitable peroxides are described in U.S. Pat. No. 4,950,581, column 19, lines 17-25), aromatic sulfonium, phosphonium or iodonium salts, as described for example in U.S. Pat. No. 4,950,581, column 18, line 60 to column 19, line 10.

The photopolymerizable compositions contain the photoinitiator appropriately in an amount of from 0.05 to 15% by weight, preferably from 0.1 to 5% by weight, based on the composition. The stated amount of photoinitiator is based on the sum of all of the added photoinitiators, if mixtures thereof are used, i.e. both onthe photoinitiator (B) and on the photoinitiators (B)+(E).

In certain cases it may be of advantage to use mixtures of two or more of the photoinitiators of the formula I; it is advantageous, for example, to use mixtures obtained directly in the preparation. It is of course also possible to use mixtures with known photoinitiators (E), examples being mixtures with camphorquinone, benzophenone, benzophenone derivatives, acetophenone, acetophenone derivatives, such as ahydroxycycloalkyl phenyl ketones or 2-hydroxy-2-methyl-1-phenylpropanone, dialkoxyacetophenones, α-hydroxy- or α-amino-acetophenones, such as (4-methylthiobenzoyl)-1-methyl-1-morpholinoethane, (4-morpholino-benzoyl)-1-benzyl-1-dimethylaminopropane, 4-aroyl-1,3-dioxolanes, benzoin alkyl ethers and benzil ketals, such as benzil dimethyl ketal, phenylglyoxalates and derivatives thereof, dimeric phenylglyoxalates, peresters, for example benzophenonetetracarboxylic peresters as described for example in EP 126541, monoacylphosphine oxides, such as (2,4,6-trimethyl-benzoyl)phenylphosphine oxide, bisacylphosphine oxides, such as bis(2,6dimethoxy-benzoyl)(2,4,4-trimethylpent-1-yl)phosphine oxide, bis(2,4,6-trimethylbenzoyl)phenyl-phosphine oxide or bis(2,4,6-trimethylbenzoyl)(2,4-dipentoxyphenyl)-phosphine oxide, trisacylphosphine oxides, halomethyltriazines, e.g. 2-[2-(4-methoxyphenyl)-vinyl]-4,6-bistrichloromethyl[1,3,5]triazine, 2-(4-methoxyphenyl)-4,6-bistrichloromethyl-[1,3,5]triazine, 2-(3,4-dimethoxyphenyl)-4,6-bistrichloromethyl[1,3,5]triazine, 2-methyl-4,6-bistrichloro-methyl[1,3,5]triazine, hexaarylbisimidazole/coinitiator systems, e.g. ortho-chlorohexa-phenylbisimidazole together with 2-mercaptobenzothiazole, ferrocenium compounds or titanocenes, such as dicyclopentadienylbis(2,6-difluoro-3-pyrrolophenyl)titanium or borate photoinitiators.

The invention also provides compositions comprising as component (A) at least one ethylenically unsaturated photopolymerizable compound in emulsion or solution in water. Such radiation-curable aqueous prepolymer dispersions are available commercially in numerous variations. They are understood to comprise a dispersion of water and at least one prepolymer dispersed therein. The concentration of the water in these systems is, for example, from 5 to 80, in particular from 30 to 60% by weight. The radiation-curable prepolymer or prepolymer mixture is present, for example, in concentrations of from 95 to 20, in particular from 70 to 40% by weight. In these compositions the sum of the percentages stated for water and prepolymers is in each case 100; the auxiliaries and additives are extra in different amounts depending on the intended use.

The radiation-curable film-forming prepolymers which are in dispersion and often also in solution in water comprise monofunctional or polyfunctional ethylenically unsaturated prepolymers which are known per se for aqueous prepolymer dispersions, may be initiated by means of free radicals, and have a polymerizable double bond content of, for example, from 0.01 to 1.0 mol per 100 g of prepolymer and also have an average molecular weight of, for example, at least 400, in particular from 500 to 10 000. Depending on the intended application, however, prepolymers with higher molecular weights may also be suitable. Use is made, for example, of polyesters containing polymerizable C-C double bonds and having an acid number of not more than 10, polyethers containing polymerizable C-C double bonds, hydroxyl-containing reaction products of a polyepoxide containing at least two epoxide groups per molecule with at least one α,β-ethylenically unsaturated carboxyiic acid, polyurethane (meth)acrylates, and also acrylic copolymers containing α,β-ethylenically unsaturated acrylic radicals, as described, for example, in EP 012339. Mixtures of these prepolymers may likewise be used. Examples of further suitable prepolymers include the polymerizable prepolymers described in EP 033896, which are thioether adducts of polymerizable prepolymers having an average molecular weight of at least 600, a carboxyl group content of from 0.2 to 15% and a polymerizable C-C double bond content of from 0.01 to 0.8 mol per 100 g of prepolymer. Other suitable aqueous dispersions based on specific alkyl (meth)acrylate polymers are described in EP 041125; suitable water-dispersible, radiation-curable prepolymers comprising urethane acrylates are given, for example, in DE 2936039. As further additions, these radiation-curable aqueous prepolymer dispersions may comprise dispersing aids, emulsifiers, antioxidants, light stabilizers, dyes, pigments, fillers, e.g. talc, gypsum, silica, rutile, carbon black, zinc oxide, iron oxides, reaction accelerants, levelling agents, lubricants, wetting agents, thickeners, matting agents, defoamers, and other auxiliaries customary in coatings technology. Suitable dispersing aids include water-soluble organic compounds of high molecular mass containing polar groups, such as polyvinyl alcohols, polyvinylpyrrolidone or cellulose ethers. Emulsifiers which can be used include nonionic, and possibly also ionic, emulsifiers.

Use

In accordance with the invention, the compounds of the formula I may be used as surface-active photoinitiators for the photopolymerization of ethylenically unsaturated compounds or mixtures comprising such compounds to obtain a hardened surface having outstanding properties. The compounds of the formula I undergo orientation toward the surface of the respective formulation. The initiators of the formula (I) are not used in compositions which comprise siloxane-modified resin components, since in such compositions the accumulation at the surface is unable to occur; instead, the initiators are compatible with the formulation and are therefore readily miscible.

It is important that the photoinitiator accumulates at the surface of the formulation to be cured. As has already been described above, this is achieved by means of appropriate substituents on the photoinitiator. However, an improveme nt in the surface properties is not only achievable using such initiators just in purely photocurable systems, but is also obtained in mixed thermally/photocurable formulations. Thermal curing may take place before, during or after exposure to light.

The invention accordingly also provides a process for producing coatings having stable scratch-resistant surfaces, in which

(1) a photocurable formulation comprising

-   -   (A) an ethylenically unsaturated polymerizable compound; and     -   (B) a photoinitiator of the above formula I; is prepared;

(2) this formulation is applied to a substrate; and

(3) the formulation is cured either only by exposure to electromagnetic radiation with a wavelength ranging from 200 nm into the IR region, or by exposure to electromagnetic radiation with a wavelength ranging from 200 nm into the IR region and prior, simultaneous and/or subsequent exposure to heat.

The invention also provides a method of causing a photoinitiator to accumulate at the surface of coatings comprising ethylenically unsaturated photopolymerizable compounds, which comprises adding a surface-active photoinitiator of the formula I to the photopolymerizable mixture comprising the ethylenically unsaturated photopolymerizable compounds.

The term “from 200 nm into the IR region” denotes from 200 nm to 2500 nm, in particular from 200 nm to 1000 nm.

The term “and/or” is intended to denote that it is possible for not only one of the defined alternatives (substituents) to be present but also two or more different alternatives (substituents) of those defined together, i.e. mixes of different alternatives (substituents).

The term “at least” is intended to define one or more than one, for example one or two or three, preferably one or two.

Unless expressly described otherwise, in the description and the claims the word comprising is to be understood to include a defined subject or a defined group of subjects but without ruling out any other substances not mentioned exclusively.

The invention also provides a process as described above in which the photocurable formulation comprises as a further component at least one thermally crosslinkable compound (C) and the formulation is cured by exposure to light whose wavelength extends from 200 nm into the IR region and by prior, simultaneous and/or subsequent exposure to heat.

To the compositions that are used in the process of the invention it is also possible to add solvents or water. Where the compositions are used without solvents, they comprise, for example, powder coating formulations. Suitable solvents are solvents which are known to the person skilled in the art and are customary particularly in coatings technology. Examples are various organic solvents, such as ketones, e.g. methyl ethyl ketone, cyclohexanone; aromatic hydrocarbons, e.g. toluene, xylene or tetramethylbenzene; glycol ethers, such as diethylene glycol monoethyl ether, dipropylene glycol diethyl ether; esters, such as ethyl acetate; aliphatic hydrocarbons, such as hexane, octane, decane; or petroleum solvents, such as petroleum ether.

The compounds of the invention and mixtures thereof may also be used as free-radical photoinitiators or photoinitiating systems for radiation-curable powder coating materials. The powder coating materials may be based on solid resins and monomers containing reactive double bonds, such as maleates, vinyl ethers, acrylates, acrylamides and mixtures thereof. A free-radically UV-curable powder coating. material may be formulated by mixing unsaturated polyester resins with solid acrylamides (e.g. methylacrylamidoglycolate methyl ester) and a free-radical photoinitiator of the invention, as described for example in the paper “Radiation Curing of Powder Coating”, Conference Proceedings, Radtech Europe 1993 by M. Wittig and Th. Gohmann. Free-radically UV-curable powder coating materials may also be formulated by mixing unsaturated polyester resins with solid acrylates, methacrylates or vinyl ethers and a photoinitiator (or photoinitiator mixture) of the invention. The powder coating materials may also include binders, as described for example in DE 4228514 and EP 636669. The powder coating formulations described in EP 636669 contain, for example, a) an unsaturated resin from the group of the (semi)crystalline or amorphous unsaturated polyesters, unsaturated polyacrylates or mixtures thereof with unsaturated polyesters, particular preference being given to those derived from maleic acid or fumaric acid; b) an oligomeric or polymeric crosslinking agent containing vinyl ether-functional, vinyl ester-functional or (meth)acrylate-functional groups, particular preference being given to vinyl ether oligomers, such as divinyl ether-functionalized urethanes; c) the photoinitiator. The UV-curable powder coating materials may also comprise white or coloured pigments. For example, preferably rutile titanium dioxide may be used in concentrations of up to 50% by weight in order to give a cured powder coating possessing good hiding power. The technique normally involves applying the powder to the substrate, such as metal or wood, by electrostatic or tribostatic spraying, melting the powder by heating and, after a smooth film has formed, radiation-curing the coating with ultraviolet and/or visible light, using medium-pressure mercury lamps, metal halide lamps or xenon lamps, for example. A particular advantage of the radiation-curable powder coating materials over their thermally curable counterparts is that the flow time after melting of the powder particles may be selectively extended in order to ensure the formation of a smooth, highly glossy coating. Unlike thermally curable systems, radiation-curable powder coating materials may be formulated without the unwanted effect of a shortened lifetime in such a way that they melt at relatively low temperatures. For this reason they are also suitable as coatings for heat-sensitive substrates, such as wood or plastics.

Where the powder coating materials are not to be applied to heat-sensitive substrates, as in the case of metals (vehicle coatings), however, it is also possible to provide dual-cure powder coating formulations with the photoinitiators of the invention. The person skilled in the art knows such formulations; they are cured both thermally and by means of UV. Formulations of this kind are given, for example, in U.S. Pat. No. 5,922,473.

Besides the photoinitiators of the invention, the powder coating formulations may also comprise UV absorbers. Appropriate examples are listed later on below.

Examples of such UV absorbers and light stabilizers are

-   1. 2-(2′-HvdroxvDhenvlbenzotriazoles, for example     2-(2′-hydroxy-5′-methylphenyl)-benzo-triazole,     2-(3′,5′-di-tert-butyl-2′-hydroxyphenyl)benzotriazole,     2-(5′-tert-butyl-2′-hydroxy-phenyl)benzotriazole,     2-(2′-hydroxy-5′-(1,1,3,3-tetramethylbutyl)phenyl)benzotriazole,     2-(3′,5′-di-tert-butyl-2′-hydroxyphenyl)-5-chtoro-benzotriazole,     2-(3′-tert-butyl-2′-hydroxy-5′-methylphenyl)-5-chloro-benzotriazole,     2-(3′-sec-butyl-5′-tert-butyl-2′-hydroxyphenyl)-benzotriazole,     2-(2′-hydroxy-4′-octyloxyphenyl)benzotriazole,     2-(3′,5′-di-tert-amyl-2′-hydroxyphenyl)benzotriazole,     2-(3′,5′-bis-(α,α-dimethylbenzyl)-2′-hydroxyphenyl)benzotriazole,     2-(3′-tert-butyl-2′-hydroxy-5′-(2-octyoxycarbonyiethyl)phenyl)-5-chloro-benzotriazole,     2-(3′-tert-butyi-5′-[2-(2-ethylhexyloxy)-carbonylethyl]-2′-hydroxyphenyl)-5-chloro-benzotriazole,     2-(3′-tert-butyl-2′-hydroxy-5′-(2-methoxycarbonylethyl)phenyl)-5-chloro-benzotriazole,     2-(3′-tert-butyl-2′-hydroxy-5′-(2-methoxycarbonylethyl)phenyl)benzotriazole,     2-(3′-tert-butyl-2′-hydroxy-5′-(2-octyloxycarbonylethyl)phenyl)benzotriazole,     2-(3′-tert-butyl-5′-[2-(2-ethylhexyloxy)carbonylethyl]-2′-hydroxyphenyl)benzotriazole,     2-(3′-dodecyl-2′-hydroxy-5′-methylphenyl)benzotriazole,     2-(3′-tert-butyl-2′-hydroxy-5′-(2-isooctyloxy-carbonylethyl)phenylbenzotriazole,     2,2′-methylene-bis[4-(1,1,3,3-tetramethylbutyl)-6-benzotriazol-2-ylphenol];     the transesterification product of     2-[3′-tert-butyl-5′-(2-methoxy-carbonylethyl)-2′-hydroxyphenyl]-2H-benzotriazole     with polyethylene glycol 300; [R—CH₂CH₂—COO—CH₂CH₂]₂— where     R=3′-tert-butyl-4′-hydroxy-5′-2H-benzotriazol-2-ylphenyl,     2-[2′-hydroxy-3′-(α,α-dimethylbenzyl)-5′-(1,1,3,3-tetramethylbutyl)-phenyl]-benzotriazole;     2-[2′-hydroxy-3′-(1,1,3,3-tetramethylbutyl)-5′-(α,α-dimethylbenzyl)-phenyl]benzotriazole. -   2. 2-Hydroxvbenzophenones, for example the 4-hydroxy, 4-methoxy,     4-octyloxy, 4-decyloxy, 4-dodecyloxy, 4-benzyloxy,     4,2′,4′-trihydroxy and 2′-hydroxy-4,4′-dimethoxy derivatives. -   3. Esters of substituted and unsubstituted benzoic acids, for     example 4-tert-butyl-phenyl salicylate, phenyl salicylate,     octylphenyl salicylate, dibenzoyl resorcinol,     bis(4-tert-butyl-benzoyl) resorcinol, benzoyl resorcinol,     2,4-di-tert-butylphenyl 3,5-di-tert-butyl-4-hydroxy-benzoate,     hexadecyl 3,5-di-tert-butyl-4-hydroxybenzoate, octadecyl     3,5-di-tert-butyl-4-hydroxybenzoate,     2-methyl-4,6-di-tert-butylphenyl     3,5-di-tert-butyl-4-hydroxybenzoate.

4. Acrvlates, for example ethyl α-cyano-β,β-diphenylacrylate, isooctyl α-cyano-β,β-diphe-nylacrylate, methyl α-carbomethoxycinnamate, methyl α-cyano-β-methyl-p-methoxy-cinnamate, butyl α-cyano-β-methyl-p-methoxy-cinnamate, methyl α-carbomethoxy-p-methoxycinnamate and N-(β-carbomethoxy-β-cyanovinyl)-2-methylindoline.

5. Sterically hindered amines, for example bis(2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis(2,2,6,6-tetramethyl-4-piperidyl) succinate, bis(1,2,2,6,6-pentamethyl-4-piperidyl) sebacate, bis(1-octyloxy-2,2,6,6-tetramethyl-4-piperidyl) sebacate, bis(1,2,2,6,6-penta-methyl-4-piperidyl) n-butyl-3,5-di-tert-butyl-4-hydroxybenzylmalonate, the condensate of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, linear or cyclic condensates of N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-tert-octylamino-2,6-dichloro-1,3,5-triazine, tris(2,2,6,6-tetramethyl-4-piperidyl) nitrilotriacetate, tetrakis(2,2,6,6-tetramethyl-4-piperidyl) 1,2,3,4-butane-tetracarboxylate, 1,1′-(1,2-ethanediyl)-bis(3,3,5,5-tetramethylpiperazinone), 4-benzoyl-2,2,6,6-tetramethylpiperidine, 4-stearyloxy-2,2,6,6-tetramethylpiperidine, bis(1,2,2,6,6-pentamethylpiperidyl) 2-n-butyl-2-(2-hydroxy-3,5-di-tert-butylbenzyl)malonate, 3-n-octyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane-2,4-dione, bis(1-octyloxy-2,2,6,6-tetramethylpiperidyl) sebacate, bis(1 -octyloxy-2,2,6,6-tetramethylpiperidyl) succinate, linear or cyclic condensates of N,N′-bis-(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-morpholino-2,6-dichloro-1,3,5-triazine, the condensate of 2-chloro-4,6-bis(4-n-butylamino-2,2,6,6-tetramethylpiperidyl)-1,3,5-triazine and 1,2-bis(3-aminopropylamino)ethane, the condensate of 2-chtoro-4,6-di-(4-n-butylamino-1,2,2,6,6-pentamethylpiperidyl)-1,3,5-triazine and 1,2-bis-(3-aminopropylamino)ethane, 8-acetyl-3-dodecyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane-2,4-dione, 3-dodecyl-1-(2,2,6,6-tetramethyl-4-piperidyl)pyrrolidine-2,5-dione, 3-dodecyl-1-(1,2,2,6,6-pentamethyl-4-piperidyl)pyrrolidine-2,5-dione, a mixture of 4-hexadecyloxy- and 4-stearyloxy-2,2,6,6-tetramethylpiperidine, a condensation product of N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)hexamethylenediamine and 4-cyclohexylamino-2,6-dichloro-1,3,5-triazine, a condensation product of 1,2-bis(3-aminopropylamino)ethane and 2,4,6-trichloro-1,3,5-triazine as well as 4-butylamino-2,2,6,6-tetramethylpiperidine (CAS Reg. No. [136504-96-6]); N-(2,2,6,6-tetramethyl-4-piperidyl)-n-dodecylsuccinimide, N-(1,2,2,6,6-pentamethyl-4-piperidyl)-n-dodecyl-succinimide, 2-undecyl-7,7,9,9-tetramethyl-1-oxa-3,8-diaza-4-oxo-spiro[4.5)decane, a reaction product of 7,7,9,9-tetramethyl-2-cyclbundecyl-1-oxa-3,8-diaza-4-oxospiro[4.5]decane und epichlorohydrin, 1,1-bis(1,2,2,6,6-pentamethyl-4-piperidyloxycarbonyl)-2-(4-methoxyphenyl)ethene, N,N′-bis-formyl-N,N′-bis(2,2,6,6-tetramethyl-4-piperidyl)-hexamethylenediamine, diester of 4-methoxy-methylene-malonic acid with 1,2,2,6,6-pentamethyl-4-hydroxypiperidine, poly(methylpropyl-3-oxy-4-(2,2,6,6-tetramethyl-4-piperidyl)]siloxane, reaction product of maleic acid anhydride-α-olefin-copolymer with 2,2,6,6-tetramethyl-4-aminopiperidine or 1,2,2,6,6-pentamethyl-4-aminopiperidine.

-   6. Oxamides, for example 4,4′-dioctyloxyoxanilide,     2,2′-diethoxyoxanilide, 2,2′-dioctyloxy-5,5′-di-tert-butoxanilide,     2,2′-didodecyloxy-5,5′-di-tert-butoxanilide,     2-ethoxy-2′-ethyloxanilide, N,N′-bis(3-dimethylaminopropyl)oxamide,     2-ethoxy-5-tert-butyl-2′-ethoxanilide and its mixture with     2-ethoxy-2′-ethyl-5,4′-di-tert-butoxanilide, mixtures of o- and     p-methoxy-disubstituted oxanilides and mixtures of o- and     p-ethoxy-disubstituted oxanilides. -   7. 2-(2-Hydroxyphenyl)-1,3,5-triazines, for example     2,4,6-tris(2-hydroxy-4-octyloxyphenyl)-1,3,5-triazine,     2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,     2-(2,4-dihydroxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,     2,4-bis(2-hydroxy-4-propyloxyphenyl)-6-(2,4-dimethylphenyl)-1,3,5-triazine,     2-(2-hydroxy-4-octyloxyphenyl)-4,6-bis(4-methylphenyl)-1,3,5-triazine,     2-(2-hydroxy-4-dodecyloxyphenyl)-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,     2-(2-hydroxy-4-tridecyloxyphenyl)-4,6-bis(2,4-dimethyl-phenyl)-1,3,5-triazine,     2-[2-hydroxy-4-(2-hydroxy-3-butyloxy-propoxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine,     2-[2-hydroxy-4-(2-hydroxy-3-octyloxy-propyloxy)phenyl]-4,6-bis(2,4-dimethyl)-1,3,5-triazine,     2-[4-(dodecyloxy/tridecyloxy-2-hydroxypropoxy)-2-hydroxyphenyl]-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,     2-[2-hydroxy-4-(2-hydroxy-3-dodecyloxy-propoxy)phenyl]-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine,     2-(2-hydroxy-4-hexyloxy)phenyl-4,6-diphenyl-1,3,5-triazine,     2-(2-hydroxy-4-methoxyphenyl)-4,6-diphenyl-1,3,5-triazine,     2,4,6-tris[2-hydroxy-4-(3-butoxy-2-hydroxy-propoxy)phenyl]-1,3,5-trazine,     2-(2-hydroxyphenyl)-4-(4-methoxyphenyl)-6-phenyl-1,3,5-triazine,     2-{2-hydroxy-4-[3-(2-ethylhexyl-1-oxy)-2-hydroxypropyloxy]phenyl}-4,6-bis(2,4-dimethylphenyl)-1,3,5-triazine. -   8. Phosphites and phosphonites, for example triphenyl phosphite,     diphenyl alkyl phosphites, phenyl dialkyl phosphites,     tris(nonylphenyl) phosphite, trilauryl phosphite, trioctadecyl     phosphite, distearyl pentaerythritol diphosphite,     tris(2,4-di-tert-butylphenyl) phosphite, diisodecyl pentaerythritol     diphosphite, bis(2,4-di-tert-butylphenyl) pentaerythritol     diphosphite, bis(2,6-di-tert-butyl-4-methylphenyl) pentaerythritol     diphosphite, diisodecyloxypentaerythritol diphosphite,     bis(2,4-di-tert-butyl-6-methylphenyl) pentaerythritol diphosphite,     bis(2,4,6-tris(tert-butyl) phenyl pentaerythritol diphosphite,     tristearyl sorbitol triphosphite, tetrakis(2,4-di-tert-butylphenyl)     4,4′-biphenylene diphosphonite,     6-isooctyl-oxy-2,4,8,10-tetra-tert-butyl-12H-dibenzo[d,g]-1,3,2-dioxaphosphocin,     bis(2,4-di-tert-butyl-6-methylphenyl) methyl phosphite,     bis(2,4-di-tert-butyl-6-methylphenyl) ethyl phosphite,     6-fluoro-2,4,8,10-tetra-tert-butyl-12-methyl-dibenzo[d,g]-1     ,3,2-dioxaphosphocin, 2,2′,2″-nitrilo[triethyl     tris(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite],     2-ethyihexyl-(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl     )phosphite,     5-butyl-5-ethyl-2-(2,4,6-tri-tert-butylphenoxy)-1,3,2-dioxaphosphirane.

Furthermore, it is possible to use additives customary in the art, such as antistatics, flow improvers and adhesion promoters.

Owing to the surface activity of the compounds of the invention it is also possible to use these compounds as flow improvers, either alone or in combination with further customary flow improvers.

The invention further provides for the use of compounds of the formula I as flow improvers, alone or in combination with further, customary flow improvers.

DIN 55945 defines levelling as “the more or less pronounced capacity of a still-liquid coating itself to compensate the unevennesses which arise in the course of its application.” (cf. J. Bieleman, Lackadditive [Additives for Coatings], VCH Weinheim 1998, chapter 6). The levelling of a coating material depends greatly on its flow behaviour and on its surface tension. Flow improvers are substances which help wet coatings to become films which flow out evenly, by reducing the viscosity and/or surface tension. In the case of powder coating materials, flow improvers also lower the melt viscosity and the glass transition temperature and have an additional devolatilizing effect. Flow improvers are used to eliminate levelling defects or surface defects which detract from the overall appearance of the coating. Levelling defects or surface defects include the orange peel effect, formation of structures, cratering, fisheyes, sensitivity to draughts, substrate wetting problems, brush marks, runs, bittiness, pinholes, etc. The use of the compounds of the invention as flow improvers makes it possible to lower the surface tension. The surface tension may be calculated by determining the marginal angle of a drop of liquid on a surface (contact angle measurement).

The photopolymerizable compositions may be used for a variety of purposes: for example, as a printing ink, as a clearcoat material, as a white paint, as a chromatically pigmented paint, for wood or metal, for example, as powder coating materials, as coating material for, inter alia, paper, wood, metal or plastic, as a daylight-curable coating for the marking of buildings and roads, for photographic reproduction techniques, for holographic recording materials, for image recording techniques or for producing printing plates which can be developed with organic solvents or using aqueous alkalis, for producing masks for screen printing, as dental filling compounds, as adhesives, including pressure-sensitive adhesives, as laminating resins, as etch resists or permanent resists, both liquid and in the form of dry films, as photostructurable dielectrics, and as solder resists for electronic circuits, as resists for producing colour filters for any type of screen, or for producing structures in the production process of plasma displays and eletroluminescent displays, for the production of optical switches, optical lattices (interference grids), for the production of three-dimensional articles by mass curing (UV curing in transparent moulds) or by the stereolithography process, as described for example in U.S. Pat. No. 4,575,330, for producing composite materials (e.g. styrenic polyesters which may where appropriate contain glass fibres and/or other fibres and other auxiliaries), and of gel coats and high-film-build compositions, for the coating or sealing of electronic components, or as coatings for optical fibres. The compositions are suitable, furthermore, for the production of optical lenses, e.g. contact lenses or Fresnel lenses, and also for producing medical instruments, aids or implants..

The compositions may also be used to produce gels having thermotropic properties, as described for example in DE 19700064 and EP 678534.

The compounds of the formula I may additionally be used as initiators for emulsion, bead or suspension polymerizations or as initiators in a polymerization for the fixing of states of order of liquid-crystalline monomers and oligomers, or as initiators for the fixing of dyes on organic materials.

The photocurable compositions of the invention are suitable for example, as coating materials for substrates of all kinds, e.g. wood, textiles, paper, ceramic, glass, plastics such as polyesters, polyethylene terephthalate, polyolefins or cellulose acetate, especially in the form of films, and also metals such as Al, Cu, Ni, Fe, Zn, Mg or Co and GaAs, Si or SiO₂, to which a protective coat or—by imagewise exposure—an image is to be applied.

The substrates may be coated by applying a liquid composition, a solution or suspension to the substrate. The choice of solvent and the concentration are guided primarily by the nature of the composition and by the coating technique. The solvent should be inert, i.e. it should not enter into any chemical reaction with the components and it should be able to be removed again in the course of drying after coating. Examples of suitable solvents are ketones, ethers and esters, such as methyl ethyl ketone, isobutyl methyl ketone, cyclopentanone, cyclohexanone, N-methylpyrrolidone, dioxane, tetrahydrofuran, 2-methoxyethanol, 2-ethoxyethanol, 1-methoxy-2-propanol, 1,2-dimethoxyethane, ethyl acetate, n-butyl acetate and ethyl 3-ethoxypropionate.

The formulation is applied uniformly to a substrate by means of known coating techniques, for example by spincoating, dipping, knife coating, curtain coating techniques, brush application, spraying, especially by electrostatic spraying, and reverse roll coating, and also by electrophoretic deposition. It is also possible to apply the photosensitive layer to a temporary flexible support and then, by layer transfer via lamination, to the final substrate.

The application (coat thickness) and nature of the substrate (coat support) are dependent on the desired field of application. The dry film thickness range generally embraces values from about 0.1 μm to more than 100 μm, preferably from 0.02 to 2 cm.

A further field of use of photocuring is that of metal coating, as in the coating of metal sheets and tubes, cans or bottle closures, for example, and also photocuring on polymer coatings, for example PVC-based wall or floor coverings.

Examples of the photocuring of paper coatings are the colourless varnishing of labels, record sleeves or book covers.

The photosensitivity of the compositions of the invention generally ranges from about 200 nm to about 600 nm (UV region). Suitable radiation Is present, for example, in sunlight or light from artificial sources. Light sources employed therefore include a large number of a very wide variety of types. Both point sources and arrays (lamp carpets) are suitable. Examples are carbon arc lamps, xenon arc lamps, medium-, high- and low-pressure mercury lamps, possibly doped with metal halides (metal-halogen lamps), microwave-excited metal vapour lamps, excimer lamps, superactinic fluorescent tubes, fluorescent lamps, argon incandescent lamps, flashlights, photographic floodlamps, light-emitting diodes (LEDs), electron beams and X-rays. The distance between the lamp and the substrate to be exposed may vary depending on the intended application and the type and output of the lamps, for example between 2 cm and 150 cm.

As already mentioned, curing in the process of the invention may take place solely by exposure to electromagnetic radiation. Depending on the composition of the formulation to be cured, however, thermal curing before, during or after radiation exposure is appropriate.

Thermal curing takes place in accordance with methods known to the person skilled in the art. Curing is generally carried out in an oven, e.g. a forced-air oven, on a hotplate, or by irradiation using IR lamps. Curing without auxiliaries at room temperature Is likewise possible, depending on the binder system used. The curing temperatures are generally between room temperature and 150° C., e.g. 25-150° C. or 50-150° C. In the case of powder coating materials or coil coating materials, the curing temperatures may also be higher, e.g. up to 350° C.

Where the formulation Includes thermally curable components (C),.It is additionally possible in accordance with the invention to add thermal drying catalysts or curing catalysts to the formulation as additional additives (D). Examples of possible drying catalysts, or thermal curing catalysts, are organometallic compounds, amines and/or phosphines. Organometallic compounds are, for example, metal carboxylates, especially those of the metals Pb, Mn, Co, Zn, Hf, Zr or Cu, or metal chelates, especially those of metals Al, Ti, Hf or Zr, or organometallic compounds such as organotin compounds. Examples of metal carboxylates are the stearates of Pb, Mn or Zn, the octoates of Co, Zn or Cu, the naphthenates of Mn and Co or the corresponding linoleates or tallates. Examples of metal chelates are the aluminium, titanium or zirconium chelates of acetylacetone, ethyl acetylacetate, salicylaldehyde, salicylaldoxime, o-hydroxyacetophenone or ethyl trifluoroacetylacetate and the alkoxides of these metals. Examples of organotin compounds are dibutyltin oxide, dibutyltin dilaurate and dibutyltin dioctoate. Examples of amines are, in particular, tertiary amines, such as tributylamine, triethanolamine, N-methyldiethanolamine, N-dimethylethanolamine, N-ethylmorpholine, N-methylmorpholine or diazabicyclooctane (triethylenediamine) and also the salts thereof. Further examples are quaternary ammonium salts, such as trimethylbenzylammonium chloride. As curing catalysts it is also possible to use phosphines, such as triphenylphosphine. Suitable catalysts are described, for example, as well in J. Bieleman, Lackadditive [Additives for Coatings], Wiley-VCH Verlag GmbH, Weinheim, 1998, page 244-247. Examples are sulfonic acids, such as p-toluenesulfonic acid, dodecylbenzenesulfonic acid, dinonylnaphthalenesulfonicacid or dinonylnaphthalenedisulfonic acid. For example, it is also possible to use latent or blocked sulfonic acids, where the blocking of the acid may be ionogenic or non-ionogenic.

Such catalysts are used in the concentrations known to the person skilled in the art and customary in that art.

The invention also provides a process for photopolymerizing non-volatile monomeric, oligomeric or polymeric compounds containing at least one ethylenically unsaturated double bond, which comprises exposing a composition as described above to electromagnetic radiation in the range from 200 to 600 nm.

The invention additionally provides for the use of the above-described composition and to a process for producing pigrmented and unpigmented paints and vamishes,. powder coating materials, gel coats, composite materials or glass fibre cable coatings.

The invention likewise provides a coated substrate coated on at least one surface with a composition as described above.

The examples which follow illustrate the invention, but do not indicate any intention that the invention be restricted to the examples.

EXAMPLES Example 1

Formula 1: R=radical of the formula II, R₁, R₂, R₃, R₄, R₅=H, s=1, Y=—CH₂—CH(OH)—CH₂—O—(CH₂)₃—, A=radical of the formula III, R₁₃, R₁₅, R₁₆, G₁, G₂=CH₃, n=p=1, m=0.

Formula 2: R=radical of the formula II, R₁, R₂, R₃, R₄, R₅=H, s=1, Y=—CH(CH₂—OH)—CH₂—O—(CH₂)₃—, A=radical of the formula III, R₁₃, R₁₅, R₁₆, G₁, G₂=CH₃, n=p=1, m=0.

A mixture of 1 equivalent of benzoylformic acid, 1.1 equivalent of (3-glycidoxypropyl)pentamethyldisiloxane and 0.11 equivalent toluenesulfonic acid monohydrate in toluene is heated to reflux for 22 hours. Evaporation of the solvent, chromatography (eluent: 19:1 to 5:1 hexane /ethyl acetate) gave the products mixture as a colorlessliquid (1.09 g, 40%).

¹H-NMR (CDCl₃) [ppm]: 8.04 (m, 2 H arom.); 7.66 (m, 1 H arom.); 7.52 (m, 2 H arom.); 4.46 (AB syst., 2×0.66 H, Ph—C(O)—C(O)—O—CH ₂—); 4.14 (m, 1 H, —CH(OH)—); 3.95 (m, 2×0.33 H, Ph—C(O)—C(O)—O—CH ₂—); 3.77-3.54 (m, 2 H. Ph—C(O)—C(O)—O—CH₂—CH(OH)—CH ₂—); 3.47 (m, 2 H, —OCH ₂—(CH₂)₂—Si—); 2.57 (br.s., 1 H, OH); 1.60 (m, 2 H, —OCH₂—CH ₂-CH₂—Si—); 0.50 (m, 2 H, —OCH₂—CH₂—CH ₂—Si—); 0.20-0.01 (m, 15 H, 5 Si—CH₃). m/z (El-Cl): 413 (MH⁺).

Example 2

Formula 1: R=radical of the formula II, R₁, R₂, R₃, R₄, R₅=H, s=1, Y==—CH₂—CH(OH)—CH₂—O—(CH₂)₃—, A=radical of the formula III, R₁₃, R₁₅, R₁₆, G₁=CH₃, G₂=—(CH₂)₃—CH₃, n=1, m=0 p=10.

Formula 2: R=radical of the formula II, R₁, R₂, R₃, R₄, R₅=H, s=1, Y==—CH(CH₂—OH)—CH₂—O—(CH₂)₃—, A=radical of the formula III, R₁₃, R₁₅, R₁₆, G₁=CH₃, G₂=—(CH₂)₃—CH₃, n=1, m=0 p=10.

The compound of Example 2 is obtained according to the method described in Example 1, using 1 molar equivalent of benzoylformic acid, 1.1 equivalent of mono-(2,3-epoxy)propylether terminated polydimethylsiloxane (MCR-E11 from ABCR) and 0.11 molar equivalent of toluenesulfonic acid monohydrate. Evaporation of the solvent, chromatography (eluent: 19:1 to 5:1 hexane lethyl acetate) gave the products mixture as a colorless liquid (2.04 g, 21%).

¹H-NMR (CDCl₃) [ppm]: 8.04 (m, 2 H arom.); 7.66 (m, 1 H arom.); 7.50 (m, 2 H arom.); 4.46 (d, J=3, 2×0.66 H. Ph—C(O)—C(O)—O—CH ₂—); 4.14 (m, 1 H, —CH(OH)—); 3.95 (m, 2×0.33 H. Ph—C(O)—C(O)—O—CH ₂—); 3.76-3.51 (m, 2 H, Ph—C(O)—C(O)—O—CH₂—CH(OH)—CH ₂—; 3.45 (m, 2 H. —OCH ₂—(CH₂)₂—Si—); 2.50 (d, 1 H, OH); 1.54 (m, 2 H, —Si—CH₂—CH₂—CH ₂—CH₃); 1.30 (m, 4 H, —OCH₂—CH ₂—CH₂—Si— and, —Si—CH₂—CH ₂—CH₂—CH₃); 0.88 (t, J=6, 3 H, , —Si—CH₂—CH₂—CH₂—CH ₃); 0.54 (m, 4 H, —OCH₂—CH₂—CH ₂—Si— and —Si—CH ₂—CH₂—CH₂—CH₃); 0.20-0.01 (m, 66 H. 22 Si—CH₃).

Example 3

Preparation of

R=radical of the formula II, R₁, R₂, R₃, R₄, R₅=H, s=2, Y=2-(bicycloheptylenyl)ethyl-, A=radical of the formula III, G₁ and G₂ are CH₃, n=2, m=0, p=8

A mixture of two equivalents of benzoylfornicacid and one equivalent of α-ω-bis-(2-nor-bornenyl)ethyl-polysiloxane (Wacker-product as described in Macromol. Sci., Pure AppI. Chem. (1996) A33(4) 439-457) in toluene is heated under reflux in the presence of an acid.

APPLICATION EXAMPLES Example A1

A clear UV-curable System based on polyurethane acrylate is prepared by mixing:

-   50 Parts Actilan® 200, difunktional urethane acrylate (Akcros) -   25 Parts SR 306, tripropylene glycol diacrylate (Cray Valley) -   15 Parts TMPTA, trimethylolpropane triacrylate (UCB) -   10 Parts SR 399, dipentaerythrol pentaacrylate (Cray Valley)

The samples were prepared by adding 3% of photoinitator.

The mixtures were applied to a white chip board, irradiated by using a UV-processor (2×80 W/cm) at a belt speed of 3 m/min. A tack free dry film with a thickness of approximately 50 μm is obtained.

30 Minutes after cure, the pendulum hardness according to König (DIN 53157) is measured. Surface energy of the coating is determined by measuring static water contact angle (θ) using a contact angle measuring system GIO from Krüss. The higher the values of the pendulum hardness measurement, the harder is the cured surface. The higher the contact angle, the better is the moisture resistance and scratch resistance. pendulum hardness Initiator [sec] water contact angle θ 3% (Example 1 + Irgacure 116 93 819 (9:1) 3% (CG 42-1558 + Irgacure 143 76 819 (9:1) Irgacure 819 available from Ciba Specialty Chem. INC. Switzerland

Example A2

A clear Dual-Cure-System based on polyurethenes is prepared by mixing:

-   21,1 Parts Desmophen® LS 2009/1, hydroxy functional polyacrylate,     (Bayer AG) Parts Roskydal® FWO 251 8C, isocyanurate based urethane     acrylate, 80% -   32.3 in butyl acetate (Bayer AG) Parts Baysilone® OL 17, flow     improver, 10% in Xylene (Bayer AG) -   0.3 Parts Modaflow®, flow improver (Monsanto) -   0.3 Parts 1-Methoxy-2-propanol, (Fluka Chemicals) -   26.0 Parts Byk® 306, flow improver (Byk-Chemie) -   0.5 Parts Roskydal® FWO 2545 E, urethane acrylate with isocyanate     groups -   11.2 (Bayer AG)

The samples were prepared by adding 3% of photoinitator and as light stabilizer 1.5% Tinuvin 400+1% Tinuvin 292

The mixtures were applied to a white coil-coat aluminum, air-dried for 5 minutes atroom temperature an heated on a hot plate at 120° C. for 10 minutes.

Irradiation is the carried out using a UV-processor (2×120 W/cm)at a belt speed of 5 m/min. A tack free dry film with a thickness of approximately 40 μm is obtained.

45 Minutes after cure, the pendulum hardness according to König (DIN 53157) is measured. Surface energy of the coating is determined by measuring static water contact angle (θ) using a contact angle measuring system G10 from Krüss. The higher the values of the pendulum hardness measurement, the harder is the cured surface. The higher the contact angle, the better is the moisture resistance and scratch resistance. pendulum hardness Initiator [sec] water contact angle θ 3% (CG 42-1556 + Irgacure 84 95 819 (9:1) 3% (CG 42-1558 + Irgacure 64 95 819 (9:1) 

1. Surface-active photoinitiators of the formula I

in which R is a radical of the formula II

or R is naphthyl, anthracyl, phenanthryl or a heterocyclic radical, the radicals naphthyl, anthracyl, phenanthryl and/or the heterocycle being unsubstituted or substituted by C₁-C₈alkyl, phenyl, OR₆, SR₇ and/or NR₈R₉, where the substituents OR₆, SR₇, NR₈R₉ may form 5- or 6-membered rings via the radicals R₆, R₇, R₈ and/or R₉ with further substituents on the naphthyl, anthracyl or phenanthryl ring or on the heterocycle or with one of the carbon atoms of the naphthyl, anthracyl or phenanthryl ring or with one of the carbon atoms of the heterocycle; and R₁, R₂, R₃, R₄ and R₅ independently of one another are hydrogen; unsubstituted C₁-C₁₂alkyl or C₁-C₁₂alkyl substituted by OH, C₁-C₄alkoxy, phenyl, naphthyl, halogen, CN and/or —O(CO)R₁₀; or are C₂-C₁₂alkyl interrupted by one or more non-successive oxygen atoms; or are OR₆; SR₇; NR₈R₉; halogen; unsubstituted or C₁-C₄alkyl- and/or C₁-C₄alkoxy-substituted phenyl, where the substituents OR₆, SR₇, NR₈Rg may form 5- or 6-membered rings via the radicals R₆, R₇, R₈ and/or R₉ with further substituents on the phenyl ring or one of the carbon atoms of the phenyl ring; R₆ and R₇ independently of one another are hydrogen; unsubstituted C₁-C₁₂alkyl or C₁-C₁₂alkyl substituted by OH, C₁-C₄alkoxy, phenyl, phenoxy and/or —O(CO)R₁₀; or are C₂-C₁₂alkyl interrupted by one or more non-successive oxygen atoms; or are unsubstituted phenyl, C₃-C₆alkenyl, cyclopentyl, cyclohexyl or naphthyl; or are C₁-C₄alkoxy-, phenyl- and/or C₁-C₄alkyl- substituted phenyl, C₃-C₆alkenyl, cyclopentyl, cyclohexyl or naphthyl; R₈ and R₉ independently of one another are hydrogen; unsubstituted C₁-C₁₂alkyl or C₁-C₁₂alkyl substituted by OH, C₁-C₄alkoxy and/or phenyl; or are C₂-C₁₂alkyl interrupted by one or more non-successive oxygen atoms; or are phenyl, —(CO)R₁₀ or SO₂R₁₁; or R₈ and Rg, together with the nitrogen atom to which they are attached, form a 5-, 6- or 7-membered ring which is uninterrupted or interrupted by —O— or —NR₁₂—; R₁₀ is C₁-C₈alkyl; unsubstituted phenyl; or phenyl substituted by C₁-C₄alkyl and/or C₁-C₄alkoxy; R₁₁ is C₁-C₁₂alkyl, unsubstituted phenyl or phenyl substituted by C₁-C₄alkyl; R₁₂ is hydrogen; unsubstituted C₁-C₈alkyl; C₁-C₈alkyl substituted by OH or C₁-C₄alkoxy; unsubstituted phenyl; phenyl substituted by OH, C₁-C₄alkyl and/or C₁-C₄alkoxy; and s is a number from 1 to 1000; A if s is 1, is a surface-active radical of the formula III

in which the units IIIa, IIIb and/or IIIc

are distributed randomly or in blocks; and G₁ is C₁-C₁₈alkyl or a radical of the formula

G₂ is C₁-C₁₈alkyl or a radical of the formula

with the proviso that, if G₂=alkyl, the radical G₂ is attached directly to the silicon atom without an oxygen bridge; R₁₃, R₁₄, R₁₅, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁ and R₂₂ independently of one another are C₁-C₁₈alkyl, phenyl, C₂-C₆hydroxyalkyl, C₂-C₆aminoalkyl or C₅-C₈cycloalkyl; R₁₆ is unsubstituted C₁-C₁₈alkyl; C₁-C₁₈alkyl substituted by hydroxyl, C₁-C₁₂alkoxy, halogen, C₃-C₈cycloalkyl and/or N(R₈)(R₉); unsubstituted phenyl; phenyl substituted by C₁-C₁₂alkyl, C₁-C₁₂alkoxy, halogen, hydroxyl and/or N(R₈)(R₉); or C₅-C₈cycloalkyl; or A if s is more than 1, is a radical of the formula III in which n is the number s; n is a number from 1 to 1000 or 0.1 to 1000 if the siloxane starting material is a mixture of oligomeric siloxanes; m is a number from 0 to 100; p is a number 0-10 000; and Y is a divalent group C₃-C₁₂cycloalkylene, C₆-C₁₂bicycloalkylene; C₁-C₆alkylene-C₃-C₁₂cycloalkylene, C₁-C₆alkylene-C₆-C₁₂bicycloalkylene or C₁-Cloalkylene interrupted by one or more non-consecutive C₃-C₁₂cycloalkylene, -U-C₃-C₁₂cycloalkylene, C₆-C₁₂bicycloalkylene or -U-C₆-C₁₂bicycloalkylene; C₁-C₁₀alkylene interrupted by one or more non-consecutive O and C₃-C₁₂cycloalkylene, -U-C₃-C₁₂cycloalkylene, C₆-C₁₂bicycloalkylene and/or -U-C₆-C₁₂bicycloalkylene;

U is U′ or U″ U′ is —(CH₂)_(a)COO—; U″ is —Si(CH₃)(CH₃)— or —(CH₂)_(a)—Si(CH₃)(CH₃)—, a is a number from 1 to 10; b is a number from 0 to 10; with the proviso that they are, however, at least 1 if the methylene group in question is between two oxygen atoms.
 2. Surface-active photoinitiators according to claim 1, wherein R is naphthyl or a radical of the formula II in which R₁, R₂, R₃, R₄ and R₅ independently of one another are hydrogen, C₁-C₄alkyl or C₁-C₄alkoxy; s is a number from 1-10, A if s is 1, is a surface-active radical of the formula III in which G₁ and G₂ have the definition indicated above, and R₁₃, R₁₄, R₁₅, R₁₆, R₁₇, R18, Ri₉, R₂₀, R₂₁ and R₂₂ independently of one another are C₁-C₄alkyl or phenyl, A if s is more than 1 is a radical of the formula III in which n is s; n is a number from 1 to 10 or 0.1 to 10, if the siloxane starting material is a mixture of oligomeric siloxanes; m is a number from 0 to 10; p is a number 0-100; y is C₁-C₆alkylene-C₃-C₁₂cycloalkylene, C₁-C₆alkylene-C₆-C₁₂bicycloalkylene; or a group selected from

a is a number from 1 to 3; b is a number from 0 to 3; with the proviso that they are, however, at least 1 if the methylene group in question is between two oxygen atoms.
 3. Surface-active photoinitiators according to claim 2, wherein R is phenyl, s is 1 or 2; A if s is 1, is a surface-active radical of the formula III in which G₁ and G₂ have the definition indicated above and R₁₃, R₁₄, R₁₅, R₁₆, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁ and R₂₂ are methyl; A if s is 2 corresponds to a radical of the formula III in which n is 2; n is a number from 1 to 10 or 0.1 to 10 if the siloxane starting material is a mixture of oligomeric siloxanes; m is 0; p is a number 0-100; Y is C₁-C₆alkylene-bicycloheptylenyl, or a group selected from

a is a number from 1 to 3; b is a number from 0 to 3; with the proviso that they are, however, at least 1 if the methylene group in question is between two oxygen atoms.
 4. A composition comprising (A) at least one ethylenically unsaturated free-radically photopolymerizable compound; and (B) at least one surface-active photoinitiator of the formula I, according to claim
 1. 5. A composition comprising (A) at least one ethylenically unsaturated free-radically photopolymerizable compound; (B) at least one surface-active photoinitiator of the formula I according to claim 1, and (C) at least one thermally crosslinkable compound and optionally comprising in addition to components (A) and (B), or (A), (B) and (C), further additives (D) and/or additional photoinitiators (E).
 6. A process for producing coatings having stable scratch-resistant surfaces, in which (1) a photocurable formulation comprising (A) an ethylenically unsaturated polymerizable compound; and (B) a photoinitiator according to claim 1; is prepared; (2) this formulation is applied to a substrate; and (3) the formulation is cured either only by exposure to electromagnetic radiation with a wavelength ranging from 200 nm into the IR region, or by exposure to electromagnetic radiation with a wavelength ranging from 200 nm into the IR region and prior, simultaneous and/or subsequent exposure to heat.
 7. A process according to claim 6, wherein the photocurable formulation comprises as a further component at least one thermally crosslinkable compound (C) and is cured by exposure to electromagnetic radiation with a wavelength ranging from 200 nm into the IR region and prior, simultaneous and/or subsequent exposure to heat.
 8. A process according to claim 7, wherein the thermally crosslinkable compound (C) is a binder based on a polyacrylate with melamine or melamine derivative, or a system based on a polyacrylate polyol and/or polyester polyol with an unblocked polyisocyanate or polyisocyanurate.
 9. A method of causing a photoinitiator to accumulate at the surface of coatings comprising ethylenically unsaturated photopolymerizable compounds, which comprises adding a surface-active photoinitiator of the formula I according to claim 1 to the photopolymerizable mixture comprising the ethylenically unsaturated photopolymerizable compounds.
 10. A process according to claim 4 for preparing pigmented and unpigmented paints and varnishes, powder coating materials, gel coats, composite materials or glass fibre cable coatings. 